- Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled
- Cossa Polimeri ESTADIENE 0460 GF Acrylonitrile Butadiene Styrene, 30% Glass Filled
Cossa Polimeri ESTADIENE 0460 GF Acrylonitrile Butadiene Styrene, 30% Glass Filled
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTADIENE |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTADIENE 0460 GF Acrylonitrile Butadiene Styrene, 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ABS with 30% glass fiber reinforcementExcellent dimensional stability, low shrinkage, good impact resistanceInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D 955 |
| Melt Flow | 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ASTM D 638 |
| Elongation at Break | 1.6 % | 1.6 % | ASTM D 638 |
| Flexural Modulus | 6.50 GPa | 943 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.600 J/cm @Temperature 0.000 °C |
1.12 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 |
| 0.700 J/cm @Temperature 23.0 °C |
1.31 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 106 °C @Load 5.00 kg |
223 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| 115 °C @Load 0.999 kg |
239 °F @Load 2.20 lb |
50°C/hr; ASTM D 1525 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
I.E.C. 695-2-1 |
Users viewing this material also viewed the following:
- Petroquimica Triunfo Trithene® CX 7020 LDPE - Cast Film
- Hong Kun Group AO 626 Antioxidant
- LATI Latilub 73/13-15T G/15 POM, 15% Glass Fiber Reinforced, PTFE Filled
- Techmer ES HiFill® PP GF/M50 CC BK 50% Glass/Mineral Filled
- Master Bond EP29LP Low Exotherm, Low Viscosity Two Component Epoxy System
- A. Schulman POLYFLAM™ FLP 3714 20% Glass Filled HDPE
- ExxonMobil LDPE LD 159AC Low Density Polyethylene Resin
- Braskem RD34U3 LLDPE Rotomolding Polyethylene
- Arlon 49100R010 0.010" (0.254 mm) Uncured Silicone Rubber with Fiberglass Substrate
- 3M 230 Crystal Clear Sealant
Copyright © lookpolymers.com All Rights Reserved