Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | <= 57.0 MPa | <= 8270 psi | ISO/R527 |
Polykemi AB SCANBLEND FS7 F20 PBT/ASA Blend, Glass Fiber-Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® CFR9111 PC COPOLYMER (Asia Pacific) Lexan* CFR9111 Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm and good flow capability. .. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® EXL1132T PC Copolymer (Asia Pacific) Lexan* EXL1132T polycarbonate (PC) siloxane copolymer resin is a UV stabilized transparent injection molding (IM) grade with extra release properties. This resin offers good low temperature (-20 C) .. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® EXL1162T PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1162T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding (IM) grade with extra release properties. This resin offers good low temperature (-20 C) ductility in c.. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® FXM121R PC PC in special effects colors. Metallic and pearlescent additives. Color package may affect performance. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® LUX9130C PC COPOLYMER Lexan* LUX9130C Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm, high flow capability and.. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® LUX9136C PC COPOLYMER (Asia Pacific) Lexan* LUX9136C Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm, high flow capability and.. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® ML3400 PC (Europe-Africa-Middle East) LEXAN ML3400 is a medium viscosity, impact modified grade with improved chemical resistance. It passes the British Standard 2495 and 5361 solvent tests. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® ML6018R PC (Asia Pacific) ML6018R is a low viscosity grade exhibiting a high impact performance over standard PC. It contains an enhanced release-agent. Opaque colours only.This data was supplied by SABIC-IP for the Asia Pac.. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® ML7672 PC (Asia Pacific) Non FR PC + GF, UV-Stabilizer, balanced flow & impact. Available in Opaque only. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP FARADEX NS0031 PC+ABS (Asia Pacific) Faradex NS0031 is a compound based on PC+ABS blend resin containing non-brominated and non-chlorinated flame retardant system, Stainless Steel. Added features of this material include: EMI/RFI Shiel.. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® CFR9131 PC COPOLYMER (Europe-Africa-Middle East) Lexan* CFR9131 Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm, high flow capability and .. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HFD1910 PC Copolymer (Europe-Africa-Middle East) 55 MFR LEXAN High Flow Ductile Copolymer, Natural colors only |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | 5 mm/min; ISO 527-1,-2 |
Lanxess Pocan® DP 7318 000000 PBT, 17% Pigment PBT, 17% white pigments, injection molding, improved light reflection, low tendency to warpInformation provided by LANXESS. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP KFP032 Acetal Copolymer (Asia Pacific) LNP* LUBRICOMP* KFP032 is a compound based on Acetal Copolymer resin containing PTFE, Silicone, Glass Fiber. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRILOY RX05497 PA 66 LNP LUBRILOY* RX05497 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRILOY RX05497 PA 66 (Asia Pacific) LNP LUBRILOY* RX05497 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® EH7020 PBT MINERAL FILLED, METALLIZABLE |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® 1731J PBT+PC (Asia Pacific) PBT+PC, Impact/chemical resistant. UV-Stabilized. Excellent physical property retention in automotive exteriors and OVAD.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® 1731J PBT+PC (Europe-Africa-Middle East) PBT+PC, Impact/chemical resistant. UV-Stabilized. Excellent physical property retention in automotive exteriors and OVAD.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL HNA033 PPE+HIPS (Asia Pacific) Noryl* HNA033 resin is an unfilled modified polyphenylene ether resin designed to withstand several cycles in an autoclave. This resin is suitable for multiple conversion routes and is available in.. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL HNA055 PPE+HIPS (Asia Pacific) >PPE+PS-HI< Autoclavable engineering thermoplastic. Biocompatible per ISO10993 (color dependent). |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL NH5120 PPE+PS Noryl* NH5120 Resin is an unreinforced blend of Polyphenylene Ether(PPE) + Polystyrenre resin. The material offers a good balance of heat, flow, hydrolytic stability, and non-halogenated V1 flame re.. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GTX GTX918WR PPE+PS+PA High flow PPE+PS+PA for under-the-hood and electrical applications. With mold release |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Noryl GTX GTX918WR PPE+PS+PA (Asia Pacific) High flow PPE+PS+PA for under-the-hood and electrical applications. With mold releaseThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer CP0436G40CL Glass Reinforced |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® FXG154 PC (Asia Pacific) FXG154 is a Lexan PC grade with the Diamond effect. Color Package may affect properties, Application testing always recommended. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® FXG154 PC (Europe-Africa-Middle East) FXG154 is a Lexan PC grade with the Diamond effect. Color Package may affect properties, Application testing always recommended.This data was supplied by SABIC-IP for the Europe-Africa-Middle East r.. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® ML1661 PC Copolymer (Asia Pacific) Medium-flow impact-modified light-shielding high-flow-ductile PC copolymer. Available in white color only. |
|||
Tensile Strength at Break | 57.0 MPa | 8270 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON ME006 PP LNP STAT-KON* ME006 is a compound based on Polypropylene resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive. |