SABIC Innovative Plastics Lexan® ML1661 PC Copolymer (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® ML1661 PC Copolymer (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Medium-flow impact-modified light-shielding high-flow-ductile PC copolymer. Available in white color only.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Melt Flow | 12 g/10 min @Load 1.20 kg, Temperature 300 °C |
12 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 113 % | 113 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Modulus | 2.10 GPa | 305 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 6.50 J/cm | 12.2 ft-lb/in | ASTM D256 |
| 6.10 J/cm @Temperature -30.0 °C |
11.4 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 66.0 J @Temperature 23.0 °C |
48.7 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C @Thickness 3.20 mm |
226 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Plastcom PLASTALEN® PQ 81 T 10 Polypropylene reinforced with mineral filler
- Raschig Group MELOPLAS® 182 MF
- Chevron Phillips 5625 LDPE Case Shrink and Bundling Film Resin (discontinued **)
- Eastman M3018-P Polyethylene (discontinued **)
- Techmer ES HiFill® PP GF20 CC LE 20% Glass Filled
- A. Schulman POLYFORT™ FPP 4529 Mineral Filled Copolymer Polypropylene
- DuPont Performance Polymers Zytel® HTN 54G35HSLR BKB336 Polyphthalamide (PPA)
- Fainplast Compounds KL 92/3 Flexible PVC, Insulation for High Temperatures Lead Free
- Ashley Polymers Ashlene® 925LS-23G Nylon 12, 23% Glass Reinforced
- Colorite Polymers 8007SF General Purpose Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved