SABIC Innovative Plastics Lexan® FXG154 PC (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® FXG154 PC (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FXG154 is a Lexan PC grade with the Diamond effect. Color Package may affect properties, Application testing always recommended.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D 792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.090 %
0.090 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.15 %

@Temperature 23.0 °C
0.15 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 2.0 g/10 min

@Load 5.00 kg,
Temperature 220 °C
2.0 g/10 min

@Load 11.0 lb,
Temperature 428 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
2.5 g/10 min

@Load 3.80 kg,
Temperature 200 °C
2.5 g/10 min

@Load 8.38 lb,
Temperature 392 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 54.0 MPa
7830 psi
5 mm/min; ISO 527
57.0 MPa
8270 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 58.0 MPa
8410 psi
Type I, 5 mm/min; ASTM D 638
61.0 MPa
8850 psi
5 mm/min; ISO 527
Elongation at Break 39 %
39 %
Type I, 5 mm/min; ASTM D 638
75 %
75 %
5 mm/min; ISO 527
Elongation at Yield 5.9 %
5.9 %
Type I, 5 mm/min; ASTM D 638
6.2 %
6.2 %
5 mm/min; ISO 527
Tensile Modulus 2.43 GPa
352 ksi
1 mm/min; ISO 527
2.68 GPa
389 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 94.0 MPa
13600 psi
2 mm/min; ISO 178
98.0 MPa
14200 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.34 GPa
339 ksi
2 mm/min; ISO 178
2.39 GPa
347 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 1.42 J/cm

@Temperature -30.0 °C
2.66 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
7.52 J/cm

@Temperature 23.0 °C
14.1 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Impact Test 62.0 J

@Temperature 23.0 °C
45.7 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 129 °C
264 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
133 °C

@Thickness 3.20 mm
271 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 147 °C
297 °F
Rate B/50; ISO 306
149 °C
300 °F
Rate B/120; ISO 306
153 °C
307 °F
Rate B/50; ASTM D 1525