SABIC Innovative Plastics Lexan® ML7672 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® ML7672 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Non FR PC + GF, UV-Stabilizer, balanced flow & impact. Available in Opaque only.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.300 % | 0.300 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.20 % | 0.20 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 4.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
4.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 52.0 MPa | 7540 psi | Type I, 5 mm/min; ASTM D638 |
| 57.0 MPa | 8270 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.8 % | 1.8 % | 5 mm/min; ISO 527 |
| 5.0 % | 5.0 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 0.30 % | 0.30 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 5.20 GPa | 754 ksi | 5 mm/min; ASTM D638 |
| 5.63 GPa | 817 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 99.0 MPa | 14400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 100 MPa | 14500 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 4.86 GPa | 705 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 5.48 GPa | 795 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 2.40 J/cm | 4.50 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | 80*10*4; ISO 180/1A |
| Charpy Impact, Notched | 1.90 J/cm² | 9.04 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 28.0 J @Temperature 23.0 °C |
20.7 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 27.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 69.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 69.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 143 °C | 289 °F | Rate B/50; ASTM D1525 |
| 143 °C | 289 °F | Rate B/50; ISO 306 | |
| 145 °C | 293 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- Parker Chomerics PORCUPINE METALASTIC® Gasketing Wire Mesh EMI Gasket Selection Guide
- SABIC Innovative Plastics NORYL WCD825 PPE-TPE (Asia Pacific)
- SABIC Innovative Plastics ULTEM 2210K PEI (Asia Pacific)
- Teknor Apex APEX® 155 Polyvinyl Chloride, Flexible
- UBE UBEPOL BR150 Synthetic Rubber (Compound)
- Westlake Hifor Xtreme SC74844 Linear Low Density Polyethylene
- ExxonMobil Exceed™ 1018KA Metallocene Polyethylene Resin
- DuPont™ Bynel® 50E662 Anhydride Modified Polypropylene
- Eurostar Starflam AFR682B1 PA66, Mineral Reinforced, Flame Retardant, Injection Molding
Copyright © lookpolymers.com All Rights Reserved