SABIC Innovative Plastics Valox® EH7020 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® EH7020 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
MINERAL FILLED, METALLIZABLE
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.014 - 0.016 cm/cm @Thickness 1.50 - 3.20 mm |
0.014 - 0.016 in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
| 0.015 - 0.016 cm/cm @Thickness 3.20 - 4.60 mm |
0.015 - 0.016 in/in @Thickness 0.126 - 0.181 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.013 - 0.014 cm/cm @Thickness 1.50 - 3.20 mm |
0.013 - 0.014 in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
| 0.014 - 0.015 cm/cm @Thickness 3.20 - 4.60 mm |
0.014 - 0.015 in/in @Thickness 0.126 - 0.181 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 57.0 MPa | 8270 psi | Type I, 5 mm/min; ASTM D638 |
| Flexural Strength | 103 MPa | 14900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.13 GPa | 599 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.89 J/cm | 7.29 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 55.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
31.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 187 °C @Thickness 6.40 mm |
369 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C @Thickness 6.40 mm |
221 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 3.1 @Frequency 50.0 - 60.0 Hz |
3.1 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | |
| Dielectric Strength | 16.9 kV/mm @Thickness 3.20 mm |
429 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.0039 @Frequency 50.0 - 60.0 Hz |
0.0039 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| 0.014 @Frequency 1.00e+6 Hz |
0.014 @Frequency 1.00e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Nilit FRIANYL B63 GV25 Nylon 6 for injection molding, 25% glass fiber reinforced
- Ferro CF 8463 Low-Temperature Sealing
- Manifattura Cattaneo VESPEL® SP1 Polyimide
- Lanxess Durethan® BKV 140 DUS008 000000 Nylon 6, 40% Glass Fiber
- Haysite 14200 Polyester BMC, 15% Glass Reinforced
- Dow Corning SILASTIC® LSR 9151-200P PARTS A&B
- DuPont Teijin Films Mylar® OL22 Polyester Film, 100 Gauge
- Buckeye Polymers BP FLEX D6512 BLK Thermoplastic Polyolefin
- Axiall 22850 Coax & Telecom Flexible PVC
Copyright © lookpolymers.com All Rights Reserved