Polymer Property : Tensile Strength at Break = 6090 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	42.0 MPa	6090 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Lexan® FL900P PC (Europe-Africa-Middle East) Foamable LEXAN, various weight reductions at 6.4 mm. Offers load bearing capability at elavated temp., Combines rigidity, impact & toughness.This data was supplied by SABIC-IP for the Europe-Africa-..
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
3M Dyneon™ PVDF 1010/0001 Polyvinylidene Fluoride (discontinued **) Polyvinylidene Fluoride (PVDF) is ideal for multiple applications across a wide array of industries. Widely used in the chemical process industry, wire and cable industry, semiconductor industry, an..
Tensile Strength at Break	42.0 MPa	6090 psi	0.025" extruded film; DIN 53504
Huntsman IROGRANÂ® PS455-200 TPU-Polyester Introduction: IROGRAN PS455-200 is a polyester based thermoplastic polyurethane intended for extrusion applications. IROGRAN PS455-200 is part of the HUNTSMAN film and sheet product range and offers..
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DL003P PC LNP LUBRICOMP* DL003P is a compound based on Polycarbonate resin containing 15% PTFE. Added features of this material include: Exceptional Processing, Internally Lubricated.
Tensile Strength at Break	42.0 MPa	6090 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL V095 PPE+PS (Europe-Africa-Middle East) Noryl* V095 resin is a modified PPE-PS blend that exhibits an excellent balance of non chlorinate, non brominate flame retardance, medium heat/high flow and low specific gravity for light weight par..
Tensile Strength at Break	42.0 MPa	6090 psi	ISO 527 Type 1A
Solvay TECHNYLÂ® C 536XT PA6, Conditioned Description: TECHNYLÂ® C 536XT is an unreinforced polyamide 6, high viscosity, for extrusion blow molding. This product is available in natural color.Benefits: The product offers a good processing..
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRILOY Z2000 PPO LNP* LUBRILOY* Z2000 is a compound based on PPO resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.
Tensile Strength at Break	42.0 MPa	6090 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® 357 PBT+PC PC/PBT, Unreinforced, impact modified, UL94V-0 rated. Applications like bobbins, switches and enclosures.
Tensile Strength at Break	42.0 MPa	6090 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® ENH3500 PBT (Asia Pacific) Unfilled PBT, Non-Brominated & Non-Chlorinated Flame Retardant
Tensile Strength at Break	42.0 MPa	6090 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics XenoyÂ® ENH2900 PBT+PC (Asia Pacific) Xenoy* ENH2900 is a Non-Braominated, Non Chlorinated flame retarded PC/PBT resin with good flow, high impact and excellent chemical resistance. It was designed quite suitable for E&E housing applic..
Tensile Strength at Break	42.0 MPa	6090 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics XenoyÂ® X3108UV PBT+PC (Europe-Africa-Middle East) Unreinforced, UV-stabilized, flame retardant, impact modified PBT+PC with V0 at 0.8mm thickness. For interior and exterior applications like wall switches and electrical enclosures.This data was sup..
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS LNP* STAT-LOY* AF3009 is a compound based on ABS resin containing 10% Glass Fiber. Added features of this material include: Antistatic, Flame Retardant.
Tensile Strength at Break	42.0 MPa	6090 psi	ISO 527
SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS LNP* STAT-LOY* AF3009 is a compound based on ABS resin containing 10% Glass Fiber. Added features of this material include: Antistatic, Flame Retardant.
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS (Asia Pacific) LNP* Stat-loy* AF3009 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber, Flame Retardant. Added features of this material include: Antistat, Flame Retardant.
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP KZ004 Acetal Copolymer (Asia Pacific) LNP* THERMOCOMP* KZ004 is a compound based on Acetal Copolymer resin containing Glass Fiber, Milled Glass.
Tensile Strength at Break	42.0 MPa	6090 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP NX07354 PC+ABS (Asia Pacific) This is a PC/ABS compound, a good candidate for Laser Direct Structuring applications.
Tensile Strength at Break	42.0 MPa	6090 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics XenoyÂ® X3108UV PBT+PC (Asia Pacific) Unreinforced, UV-stabilized, flame retardant, impact modified PBT+PC with V0 at 0.8mm thickness. For interior and exterior applications like wall switches and electrical enclosures.This data was sup..
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DB008ERP PC (Asia Pacific) LNP* Thermocomp* DB008ERP is a compound based on Polycarbonate resin containing Glass Bead. Added features of this material include: Easy Molding, Mold Release.
Tensile Strength at Break	42.0 MPa	6090 psi	ISO R 527
Stir SpA RH I P (PVC) Application: Spiral extrusion - various profilesInformation provided by STIR SpA
Tensile Strength at Break	42.0 MPa	6090 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP MF002S PP LNP* Thermocomp* MF002S is a compound based on Polypropylene resin containing 10% Glass Fiber. Added features of this material include: Heat Stabilized.
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
Denka MALECCA K-100 ABS A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de..
Tensile Strength at Break	42.0 MPa	6090 psi	50mm/min; ASTM D638
Denka TH-11 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a..
Tensile Strength at Break	42.0 MPa	6090 psi	50mm/min; ASTM D638
Denka TP-801 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a..
Tensile Strength at Break	42.0 MPa	6090 psi	Conditioned 15 days at 23°C - 50% RH; ASTM D638
Arkema Group Pebax® MX 1205 SA 01 MED Polyether Block Amide (PEBA) Polyether block amide PEBAX® MX 1205 SA 01 MED is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This grade offers the highest quality and it is specially designed to mee..
Tensile Strength at Break	42.0 MPa	6090 psi	ASTM D638
Braskem HB 0155 HDPE Blow Molding Polyethylene Applications: Large containers from 60 to 200 litersInformation provided by Braskem
Tensile Strength at Break	42.0 MPa	6090 psi	ISO 527-1
Barlog Plastics KEBAFLEX U A 75 ST B01 natural TPU, Shore A75, natural TPUInformation provided by BARLOG plastics GmbH.
Tensile Strength at Break	42.0 - 50.0 MPa	6090 - 7250 psi	5 mm/min.; IS 867-1963
Amity Thermosets ATI 101 Phenolic Molding Organic Filler, Injection Molded Characteristics:Electrical low loss Good mechanical strengthHigh electrical insulationGood mechanical strengthGlossy surfaceLow water absorptionColor-blackVery soft flow Applications: Electric swit..
Tensile Strength at Break	42.0 MPa	6090 psi	50mm/min; ASTM D638
3M Dyneon™ PVDF 6012/0000 Polyvinylidene Fluoride 3M™ Dyneon™ PVDF 6012/0000 is ideal for multiple applications across a wide array of industries. Widely used in the chemical process industry, wire and cable industry, semiconductor industry, and ..
Tensile Strength at Break	42.0 MPa	6090 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL PX2060 PPE+PS (Europe-Africa-Middle East) Noryl* PX2060 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and high flow , this resin also uses non-chlorinated, non-brominated FR ..