Denka MALECCA K-100 ABS

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer Denka
Trade Name MALECCA
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Denka MALECCA K-100 ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had defects in terms of moldability, thermal stability, and impact resistance.ApplicationsMobile phonesvehicle-mounted audio equipmentautomotive interior componentshome electric appliancesOA equipment, etc.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Density 1.06 g/cc
0.0383 lb/in³
ISO 1183
Melt Flow 8.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
8.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 113
113
ISO 2039-2
114
114
ASTM D785
Tensile Strength at Break 42.0 MPa
6090 psi
ASTM D638
48.0 MPa
6960 psi
50mm/min; ISO 527-2
Tensile Strength, Yield 38.0 MPa
5510 psi
ISO 527-2
Elongation at Break 28 %
28 %
ISO 527-2
Tensile Modulus 2.50 GPa
363 ksi
1mm/min; ISO 527-1
Flexural Strength 74.0 MPa
10700 psi
15mm/min; ASTM D790
76.0 MPa
11000 psi
ISO 178
Flexural Modulus 2.35 GPa
341 ksi
15mm/min; ASTM D790
2.45 GPa
355 ksi
2mm/min; ISO 178
Izod Impact, Notched 1.96 J/cm

@Temperature 23.0 °C
3.67 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Charpy Impact, Notched 2.00 J/cm²
9.52 ft-lb/in²
ISO 179-2
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
ISO 75-2
103 °C
217 °F
ASTM D648
Vicat Softening Point 113 °C
235 °F
50N; ISO 306
Flammability, UL94 HB
HB