Amity Thermosets ATI 101 Phenolic Molding Organic Filler, Injection Molded

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic
Manufacturer	Amity Thermosets
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Amity Thermosets ATI 101 Phenolic Molding Organic Filler, Injection Molded.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Characteristics:Electrical low loss Good mechanical strengthHigh electrical insulationGood mechanical strengthGlossy surfaceLow water absorptionColor-blackVery soft flow Applications: Electric switchgear components ( eg. relays ) Telecommunication equipment partsElectronic equipment partsAutomotive ( electronic and electrical ) parts Medium tension pulleysHigh gloss toilet seatsBig meter coversCircuit breaking switchesCoffee machine basesAutomobile light and signaling switches Moulding which ought to have overall good propertiesSolenoid switch covers, knobs and tops (superior quality), etc. Information provided by Amity Thermosets Limited

Physical Properties	Metric	English	Comments
Density	1.32 - 1.38 g/cc	0.0477 - 0.0499 lb/in³	Molding; IS 867-1963
Apparent Bulk Density	0.600 - 0.680 g/cc	0.0217 - 0.0246 lb/in³	IS 867-1963
Water Absorption	0.25 - 0.37 %	0.25 - 0.37 %	IS 13411-1993
Linear Mold Shrinkage	0.0070 - 0.010 cm/cm	0.0070 - 0.010 in/in	IS 13411-1992

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	42.0 - 50.0 MPa	6090 - 7250 psi	5 mm/min.; IS 867-1963
Shear Strength	67.0 - 70.0 MPa	9720 - 10200 psi	IS 867-1963
Izod Impact, Notched	0.200 - 0.300 J/cm	0.375 - 0.562 ft-lb/in	IS 13411-1992

Electrical Properties	Metric	English	Comments
Volume Resistivity	3.2e+11 - 3.2e+12 ohm-cm	3.2e+11 - 3.2e+12 ohm-cm	IS 3396-1979
Surface Resistance	3.2e+10 - 3.2e+11 ohm	3.2e+10 - 3.2e+11 ohm	IS 3396-1979
Dielectric Strength	5.00 - 7.00 kV/mm @Temperature 90.0 °C	127 - 178 kV/in @Temperature 194 °F	IS 2584-1963

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	65.0 - 85.0 °C	149 - 185 °F
Front Barrel Temperature	85.0 - 95.0 °C	185 - 203 °F
Nozzle Temperature	<= 105 °C	<= 221 °F
Mold Temperature	160 - 180 °C	320 - 356 °F
Injection Pressure	98.0 - 196 MPa	14200 - 28400 psi
Hold Pressure	58.8 MPa	8530 psi
Cure Time	0.200 - 0.333 min	0.00333 - 0.00556 hour	per mm
Shelf Life	12.0 Month	12.0 Month	10-25°C