SABIC Innovative Plastics Valox® ENH3500 PBT (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® ENH3500 PBT (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unfilled PBT, Non-Brominated & Non-Chlorinated Flame Retardant
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.018 - 0.028 cm/cm | 0.018 - 0.028 in/in | on Tensile Bar; SABIC Method |
| Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 250 °C |
20 g/10 min @Load 4.76 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 38.0 MPa | 5510 psi | 50 mm/min; ISO 527 |
| 42.0 MPa | 6090 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | 50 mm/min; ISO 527 |
| 44.0 MPa | 6380 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 8.0 % | 8.0 % | 50 mm/min; ISO 527 |
| 10 % | 10 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 3.0 % | 3.0 % | Type I, 50 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 3.15 GPa | 457 ksi | 5 mm/min; ASTM D638 |
| 3.20 GPa | 464 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 70.0 MPa | 10200 psi | 2 mm/min; ISO 178 |
| 77.0 MPa | 11200 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.70 GPa | 392 ksi | 2 mm/min; ISO 178 |
| 2.75 GPa | 399 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.400 J/cm | 0.749 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| 50.0 kJ/m² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 60.0 °C @Thickness 3.20 mm |
140 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 170 °C | 338 °F | Rate B/120; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | >= 600 V | >= 600 V | UL 746A |
| 600 V | 600 V | IEC 60112 |
Users viewing this material also viewed the following:
- PSM Industries Pacific Sintered Metals High Carbon Steel F-244-S(HT) Powdered Metal
- Flint Hills AP7810-HS Polypropylene Ultra High Impact Copolymer
- Kuraray Genestarâ„¢ N1002A-M41 Nylon
- Lanxess Durethan® B 30 S FN40 000000 Nylon 6
- Stir SpA C 2071 AT (PVC)
- A. Schulman PP 1667-01 Polypropylene Natural Homopolymer Polypropylene
- ChevronTexaco Geotex® LA SAE 30
- LNP Lubricomp® OCL-4036 Polyphenylene Sulfide, Carbon Fiber Reinforcement, PTFE Lubricant (discontinued **)&l
- A.D. Compound Adene NCHA Homopolymer 25% CaCO3 Filled Polypropylene
- RheTech Products GC20P600-01UV 20% Glass Fiber Reinforced Polypropylene, Chemically Coupled, UV Stabilized, Black
Copyright © lookpolymers.com All Rights Reserved