Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | >= 38.0 MPa | >= 5510 psi | ASTM D638 |
NIZHNEKAMSKNEFTEKHIM 535 General Purpose Polystyrene Grade 535 is a high heat crystal polystyrene designed for injection molding, extrusion and blow molding. It is used for electronic packaging, extruded light diffusers and office accessories.Informa.. |
|||
Tensile Strength at Break | >= 38.0 MPa | >= 5510 psi | ASTM D638 |
NIZHNEKAMSKNEFTEKHIM 585 General Purpose Polystyrene Grade 585 is a high molecular weight, low melt-flow crystal polystyrene. This polymer is tailored for extruded foam applications such as egg cartons, meat trays and food service. It is also suited.. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DBL32 PC LNP* Lubricomp* DBL32 is a compound based on Polycarbonate resin containing 10% Glass Beads and 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO R 527 |
Fainplast Compounds RI 52 Rigid PVC, Injection Molding Fittings for building trade |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO R 527 |
Fainplast Compounds RKS 212/W Rigid PVC, Antishock Extrusion Lead Free Outdoor antishock profiles |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO 527 |
SABIC Innovative Plastics LNP Lubricomp KX99792 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KX99792 is a compound based on Acetal Copolymer resin containing Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the .. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO 527 |
SABIC Innovative Plastics LNP Lubricomp KX99792 Acetal Copolymer LNP* Lubricomp* KX99792 is a compound based on Acetal Copolymer resin containing Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the .. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | (Wire/Cable), break Aged 1 week at 135°C |
SABIC Innovative Plastics ULTEM STM1500 PEI Copolymer Siloxane polyetherimide block copolymer. Wire and cable use. Strength and flexibility. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® EXXY0113 PBT (Asia Pacific) Blow Moldable Impact modified XENOYThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP C7410 PC+ABS (Asia Pacific) LNP* Thermocomp* C7410 compound is a talc-filled PC+ABS, nonhalogenated FR for thinwall molding applications. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL PVX524 PPE PREVEX* PVX524 resin is a high flow, non FR grade, 100 C HDT |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO R 527 |
Stir SpA RF 1000A (PVC) Application: Extrusion shock resistant profiles for windowsInformation provided by STIR SpA |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM D638 |
Toyobo PELPRENE™ P150B Polyester TPE Features: Polyester TPEInformation provided by Toyobo. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM D638 |
Eastman Eastar DN001HF Copolyester Applications:DisplaysPersonal care and CosmeticsProduct Description: Eastar Copolyester DN001HF has excellent flow characteristics while maintaining superior mechanical properties. It is easy to p.. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO 527-1/-2 |
DSM Arnitel® EL740 Polyether Ester Elastomer (European and Asian Grade) Product description: Arnitel® combines the advantages of engineering thermoplastics, being easy to process with excellent mechanical properties, at the same time with the flexibility of rubbers.Arn.. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | 50 mm/min; ISO 179/2D |
Chi Mei Kibilac® PW-957 ASA Polymer Injection |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | 50mm/min; ASTM D638 |
Denka TP-803 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | chs 2.0 in/min; ASTM D638 |
Diamond Polymers DIAMALOY GLY 9020 Sheet Extrusion Grade Diamaloy GLY 9020 resin is a high-gloss, low impact grade of ASA (acrylonitrile-styrene-acrylate) with good resistance to weather aging. It has good melt strength for extrusion and thermoforming, an.. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO R 527 |
Fainplast Compounds R 220/R Rigid PVC, Extrusion Shiny rolling shutters |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | 50 mm/min; ISO 527 |
Chi Mei Polylac® PA-777D ABS - High Heat Super High Heat |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM D3759 |
3M Scotch® 8988 Filament Tape Scotch® Filament Tape 8988 is a high-performance, packaging tape reinforced with continuous glass-yarn filaments that give the tape very high tensile strength. The adhesive is a very aggressive pac.. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM D638 |
Asahi Glass Fluon® LM-740AP LM-ETFE Fluororesin Fluon®LM-ETFE combines the excellent properties in heat resistance and other mechanical properties owned by ETFE resin and the low melting point.Information provided by Asahi Glass Company, Inc. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO R 527 |
Fainplast Compounds RE 220 Rigid PVC, Extrusion Various profiles |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DBL32 PC (Asia Pacific) LNP* Lubricomp* DBL32 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP DBL32 PC (Asia Pacific) LNP* Lubricomp* DBL32 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® X6800BM PBT (Europe-Africa-Middle East) Blow moldable, impact modifed XENOY |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DBL349E PC LNP* Lubricomp* DBL349E is a compound based on Polycarbonate resin containing 20% Glass Bead, 15% PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retard.. |
|||
Tensile Strength at Break | 38.0 MPa | 5510 psi | 5 mm/min; ISO 527-1,-2 |
Ineos ABS Triax® KU2-3154 ABS + Polyamide Blend (DAM), Injection Molding Grade Triax® KU2-3154 is mineral reinforced, easy-flowing, injection molding grade, and comes in pellets. It has reduced moisture absorption and very low warpage. |