Chi Mei Kibilac® PW-957 ASA Polymer
| Category | Polymer , Thermoplastic , ASA Polymer |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Kibilac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Kibilac® PW-957 ASA Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 |
| Melt Flow | 26 g/10 min @Load 10.0 kg, Temperature 220 °C |
26 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 88.0 MPa | 12800 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 38.0 MPa | 5510 psi | 50 mm/min; ISO 179/2D |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 20 % | 20 % | 50 mm/min; ISO 527 |
| Flexural Strength | 67.0 MPa | 9720 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.90 GPa | 276 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180/1C |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 1.23 J/cm² | 5.85 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | unannealed; ISO 75 |
| 94.0 °C | 201 °F | annealed; ISO 75 | |
| Vicat Softening Point | 92.0 °C @Load 5.00 kg |
198 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 95.0 °C @Load 5.00 kg |
203 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 105 °C @Load 1.00 kg |
221 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 107 °C @Load 1.00 kg |
225 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB | HB | UL 94 |
Users viewing this material also viewed the following:
- Proto3000 Objet FullCure720 Transparent Prototyping Polymer
- Nilit FRIANYL A63 SG40 Nylon 6.6 for injection molding, 40% mineral filled
- Covestro Texin® 5286 Thermoplastic Polyurethane, Polyether-based, Medical (discontinued **)
- Shakespeare S-3 Economy Nylon Copolymer Fishing Line, 10 lb
- A. Schulman PP 3491 Polypropylene Homopolymer Polypropylene
- Beijing Chemical Industry KAIFA® 101 PBT Resin
- A. Schulman ComAlloy Aqualoy® 135 Polypropylene, Glass Reinforced, Chemically Coupled NSF, UL
- Denka VINYKON S210060 PVC, S grade for transparent extrusion molding
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR N990 Filler
- BASF Lupranate® 278 Isocyanate
Copyright © lookpolymers.com All Rights Reserved