Denka TP-803 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene

Category	Polymer , Thermoplastic , Styrene-Butadiene
Manufacturer	Denka
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Denka TP-803 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

"TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a good balance of transparency, strength and fluidity (methyl methacrylate butadiene styrene), "TE Series/CL Series," transparent ABS resins with excellent color attributes and tensile strength are available (among others).ApplicationsTX is used for:flat display substratesoptical componentsmiscellaneous goods.TP/TH are used for:food package sheeting as well as in manufacturingelectronic equipment and componentsmiscellaneous goodsTE/CL are for:electronic equipment and componentsinformation equipment componentsAV equipment, etc.

Physical Properties	Metric	English	Comments
Specific Gravity	1.10 g/cc	1.10 g/cc	ASTM D792
Density	1.082 g/cc	0.03909 lb/in³	ISO 1183
Melt Flow	3.9 g/10 min @Load 5.00 kg, Temperature 200 °C	3.9 g/10 min @Load 11.0 lb, Temperature 392 °F	ISO 1133
	61 g/10 min @Load 10.0 kg, Temperature 220 °C	61 g/10 min @Load 22.0 lb, Temperature 428 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	29	29	ISO 2039-2
Tensile Strength at Break	32.0 MPa	4640 psi	50mm/min; ISO 527-2
	38.0 MPa	5510 psi	50mm/min; ASTM D638
Elongation at Break	40 %	40 %	50mm/min; ISO 527-2
Tensile Modulus	4.30 GPa	624 ksi	50mm/min; ISO 527-1
Flexural Strength	64.0 MPa	9280 psi	ISO 178
	65.0 MPa	9430 psi	2mm/min; ASTM D790
Flexural Modulus	2.00 GPa	290 ksi	2mm/min; ISO 178
	2.01 GPa	292 ksi	2mm/min; ASTM D790
Izod Impact Resistance	13.7 J/cm²	65.2 ft-lb/in²
Charpy Impact, Notched	1.30 J/cm²	6.19 ft-lb/in²	ISO 179-2

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	63.0 °C	145 °F	ISO 75-2
	71.0 °C	160 °F	ASTM D648
Vicat Softening Point	84.0 °C	183 °F	50N; ISO 306
Flammability, UL94	HB	HB

Optical Properties	Metric	English	Comments
Haze	2.6 % @Thickness 2.00 mm	2.6 % @Thickness 0.0787 in	ISO 14782
Transmission, Visible	91 % @Thickness 2.00 mm	91 % @Thickness 0.0787 in	ISO 13468-1