SABIC Innovative Plastics LNP Lubricomp KX99792 Acetal Copoly (Asia Pacific)
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Silicone Filled |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubricomp KX99792 Acetal Copoly (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* KX99792 is a compound based on Acetal Copolymer resin containing Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.027 - 0.031 cm/cm @Time 86400 sec |
0.027 - 0.031 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.021 - 0.024 cm/cm @Time 86400 sec |
0.021 - 0.024 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO 527 |
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | ISO 527 |
| Elongation at Break | 30 % | 30 % | ISO 527 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO 527 |
| Tensile Modulus | 2.07 GPa | 300 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 48.0 MPa | 6960 psi | ISO 178 |
| Flexural Modulus | 1.70 GPa | 247 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 52.0 kJ/m² @Temperature 23.0 °C |
24.7 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.20 | 0.20 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.10 | 0.10 | ASTM D 3702 Modified |
| K (wear) Factor | 2.01 x 10-8 mm³/N-M | 1.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- NeXolve Novastrat® 400 Polyimide
- Solvay Specialty Polymers Halar® 3404DA Polyethylene, Chlorotrifluoroethylene (ECTFE) (Unverified Data**)
- Gouda Vuurvast CURON 160 H Dense Refractory Castable
- Shakespeare WN-20 diameter 0.2 mm Nylon 66 Monofilament
- UBE UBESTA® 3030U Nylon 12 (After Chloroform for 500 hours)
- CP-Polymer-Technik Wellamid® 6000 GVZ 45 HWCP 45% Glass Fiber Nylon 6, Impact Resistant, Good Surface Finish, Heat Stabilized, Dry
- Eurostar Staramide AST43 PA66, Impact Modified, Injection Molded
- Aclo Accutech Polypropylene Homopolymer HP0336T10L Talc Reinforced
- BASF Novolen® 3240 NC Polypropylene
- Asia International Enterprise (Hong Kong) 3010FW Polybutylene terephthalate
Copyright © lookpolymers.com All Rights Reserved