- HOME
- POLYMER SEARCH
- Thermoplastic
- ABS Polymer
- Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
- Chi Mei Polylac® PA-777D ABS - High Heat
Chi Mei Polylac® PA-777D ABS - High Heat
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polylac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polylac® PA-777D ABS - High Heat.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Super High Heat
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO-1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Ball Indentation Hardness | 102 MPa | 14800 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 38.0 MPa | 5510 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 13 % | 13 % | 50 mm/min; ISO 527 |
| Flexural Strength | 73.0 MPa | 10600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 1.44 J/cm @Thickness 6.35 mm |
2.70 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 1.77 J/cm @Thickness 3.17 mm |
3.32 ft-lb/in @Thickness 0.125 in |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 125 kJ/m² | 59.5 ft-lb/in² | ISO 180/1C |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 1.10 J/cm² | 5.24 ft-lb/in² | ISO 179 |
| Impact | 10.0 | 10.0 | Impact Flexural Test Notched (KJ/m²) |
| NB | NB | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 103 °C | 217 °F | unannealed; ISO 75 |
| 113 °C | 235 °F | annealed; ISO 75 | |
| Vicat Softening Point | 115 °C @Load 5.00 kg |
239 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 118 °C @Load 5.00 kg |
244 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 125 °C @Load 1.00 kg |
257 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 127 °C @Load 1.00 kg |
261 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL 94 |
Users viewing this material also viewed the following:
- MV Labs BI600 BiI3 Bismuth iodide
- Plastcom SLOVALEN PH 63 T 20 PP, 20% mineral filling
- Nilit FRIANYL B63 E Raw extruded nylon 6 for injection molding
- Multibase Multi-Flex® TPE A 4002 BLK
- Dow Corning Q3-3559 SEMIFLOWABLE TEXTILE ELASTOMER
- Arkema Group ORGASOL® 2002 EXD Nat 1 Polyamide 12, Food Contact Approved
- SABIC Innovative Plastics LNP LUBRICOMP DL002ER PC (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved