SABIC Innovative Plastics LNP LUBRICOMP DBL32 PC

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP DBL32 PC.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Lubricomp* DBL32 is a compound based on Polycarbonate resin containing 10% Glass Beads and 15% PTFE. Added features of this material include: Internally Lubricated.

Physical Properties	Metric	English	Comments
Density	1.37 g/cc	0.0495 lb/in³	ASTM D792
	1.37 g/cc	0.0495 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ASTM D955
	0.0080 cm/cm @Time 86400 sec	0.0080 in/in @Time 24.0 hour	ISO 294
Linear Mold Shrinkage, Transverse	0.0096 cm/cm @Time 86400 sec	0.0096 in/in @Time 24.0 hour	ISO 294
	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	38.0 MPa	5510 psi	ASTM D638
	38.0 MPa	5510 psi	Type I, 5 mm/min; ASTM D638
	38.0 MPa	5510 psi	ISO 527
	38.0 MPa	5510 psi	5 mm/min; ISO 527
Tensile Strength, Yield	42.0 MPa	6090 psi	ASTM D638
	42.0 MPa	6090 psi	Type I, 5 mm/min; ASTM D638
	43.0 MPa	6240 psi	ISO 527
	43.0 MPa	6240 psi	5 mm/min; ISO 527
Elongation at Break	18.2 %	18.2 %	ISO 527
	18.2 %	18.2 %	5 mm/min; ISO 527
	22.3 %	22.3 %	ASTM D638
	22.3 %	22.3 %	Type I, 5 mm/min; ASTM D638
Elongation at Yield	5.1 %	5.1 %	ISO 527
	5.1 %	5.1 %	5 mm/min; ISO 527
	5.4 %	5.4 %	ASTM D638
	5.4 %	5.4 %	Type I, 5 mm/min; ASTM D638
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D638
	2.58 GPa	374 ksi	1 mm/min; ISO 527
Flexural Strength	69.0 MPa	10000 psi	ISO 178
Flexural Modulus	2.40 GPa	348 ksi	ISO 178
	2.40 GPa	348 ksi	2 mm/min; ISO 178
	2.75 GPa	399 ksi	ASTM D790
	2.75 GPa	399 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	1.92 J/cm	3.60 ft-lb/in	ASTM D256
Izod Impact, Unnotched	15.0 J/cm	28.1 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	14.0 kJ/m²	6.66 ft-lb/in²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	105 kJ/m²	50.0 ft-lb/in²	80104; ISO 180/1U
Dart Drop, Total Energy	31.0 J	22.9 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	25.0 J	18.4 ft-lb	Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic	0.41	0.41	ASTM D3702 Modified
Coefficient of Friction, Static	0.48	0.48	ASTM D3702 Modified
K (wear) Factor	280 x 10^-8 mm³/N-M	139 x 10^-10 in³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	53.0 µm/m-°C @Temperature -40.0 - 40.0 °C	29.4 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
	54.0 µm/m-°C @Temperature -40.0 - 40.0 °C	30.0 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
CTE, linear, Transverse to Flow	59.4 µm/m-°C @Temperature -40.0 - 40.0 °C	33.0 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	60.0 µm/m-°C @Temperature -40.0 - 40.0 °C	33.3 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	139 °C	282 °F	Flatw 80104 sp=64mm; ISO 75/Bf
	142 °C @Thickness 3.20 mm	288 °F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	135 °C	275 °F	Flatw 80104 sp=64mm; ISO 75/Af
	135 °C @Thickness 3.20 mm	275 °F @Thickness 0.126 in	unannealed; ASTM D648