Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 117 MPa | 17000 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Nymax™ GMF 600 A 40 Natural Polyamide 6 (Nylon 6) The Nymax® 600 Series of mineral-reinforced nylon 6 compounds have been specifically developed to provide an excellent balance of physical property performance and durability, with improved surface.. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Nymax™ GMF 604 40 UV Black 28 Polyamide 6 (Nylon 6) The Nymax® GMF 600 Series of compounds are based upon nylon 6 resins and select combinations of glass fiber and mineral reinforcements offering a unique balance of physical property and part perfor.. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D638 |
Polymer Resources PC-G20 Polycarbonate, 20% Glass Reinforced Polycarbonate, 20% Glass ReinforcedFeatures: • Flame Retardant • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-p.. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Nymax™ GF 1200 A 13 Natural Polyamide 66 (Nylon 66) The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durabil.. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Nymax™ X GMF 604 40 UV Black 148 rev 4 Polyamide 6 (Nylon 6) The Nymax® GMF 600 Series of compounds are based upon nylon 6 resins and select combinations of glass fiber and mineral reinforcements offering a unique balance of physical property and part perfor.. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Lubricomp QCL329 PA 6/10 LNP LUBRICOMP* QCL329 is a compound based on Nylon 6/10 resin containing Carbon Fiber, Flame Retardant, PTFE. Added features of this material include: Electrically Conductive.This data was supplied.. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Lubricomp QCL329 PA 6/10 (Asia Pacific) LNP LUBRICOMP* QCL329 is a compound based on Nylon 6/10 resin containing Carbon Fiber, PTFE, Flame Retardant. Added features of this material include: Electrically Conductive.This data was supplied.. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP WFL36 PBT LNP LUBRICOMP* WFL36 is a compound based on PBT resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP WFL36 PBT (Asia Pacific) LNP LUBRICOMP* WFL36 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® HR426 PBT (Asia Pacific) AUTOMOTIVE. 30% GR, hydrolytically stable PBT. Excellent strength, stiffness and dimensional stability. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DX10311 PC (Asia Pacific) DX10311 is 30% glass fiber reinforced, impact modified polycarbonate resin. High flow and good ductility. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK3020 PC LNP* Thermocomp* Lexan_LGK3020 compound is a glass reinforced. Flame retardant. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK3020 PC (Europe-Africa-Middle East) LNP* Thermocomp* Lexan_LGK3020 compound is a glass reinforced, flame retardant material. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D638 |
PlastxWorld CEVIAN®-N GRSJ3 30% GF SAN resin Glass fiber reinforced SAN resin. These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D638 |
Chase Plastics CP Pryme® NN113GL (DAM) Nylon 66, 13% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D638 |
Chase Plastics CP Pryme® NN313L (Dry) Nylon 66, 13% Glass Fiber Reinforced, Lubricated, Recycled Content Features: LubricatedRecycled ContentForm: PelletsInformation provided by Chase Plastics. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D638 |
Chase Plastics CP Pryme® PC330GR Polycarbonate (Utility Grade), 30% Glass Fiber Reinforced, Mold Release Information provided by Chase Plastics. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | DIN EN ISO 527 |
Wolf Kunststoff ZEDEX® ZX-324V1T A3H PEEK Polymer, Reinforced Main Characteristics: High resilience; High elasticity; Low permanent deformation; Stress resistant; High strength at temperatures above 140 ° CApplications: Shipbuilding; Chemical Engineering; Aut.. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® R525H BK0201 Nylon 66, 25% Glass Reinforced, Conditioned Vydyne® R525H BK0201 is hydrolysis-resistant, 25% glass-fiber reinforced, heat-stabilized PA66 resin. Available in black, it is specifically designed to maximize the retention of physical propertie.. |
|||
Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D638 |
Polymer Resources PCSF-FRG20 Polycarbonate, 20% Glass Reinforced Structural Foam Grade Polycarbonate, 20% Glass Reinforced Structural Foam GradeFeatures: • Flame Retardant • Foamable • Self ExtinguishingProcess: Foam MoldingNotes: All physical, mechanical and thermal testing con.. |