SABIC Innovative Plastics LNP LUBRICOMP WFL36 PBT (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP WFL36 PBT (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* WFL36 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in³ | ASTM D792 |
| 1.68 g/cc | 0.0607 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0400 % | 0.0400 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0400 % | 0.0400 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.010 cm/cm @Time 86400 sec |
0.0050 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0050 - 0.010 cm/cm @Time 86400 sec |
0.0050 - 0.010 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D638 |
| 118 MPa | 17100 psi | ISO 527 | |
| Elongation at Break | 2.2 % | 2.2 % | ISO 527 |
| 2.3 % | 2.3 % | ASTM D638 | |
| Tensile Modulus | 10.34 GPa | 1500 ksi | 50 mm/min; ASTM D638 |
| 10.61 GPa | 1539 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 187 MPa | 27100 psi | ISO 178 |
| 193 MPa | 28000 psi | ASTM D790 | |
| Flexural Modulus | 10.01 GPa | 1452 ksi | ISO 178 |
| 10.16 GPa | 1474 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.83 J/cm | 12.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 42.0 kJ/m² | 20.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J | 9.59 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.57 | 0.57 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.41 | 0.41 | ASTM D3702 Modified |
| K (wear) Factor | 84.6 x 10-8 mm³/N-M | 42.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 38.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 38.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 67.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 67.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 217 °C @Thickness 3.20 mm |
423 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Fujipoly Industries Sarcon® 85U Thin-Film UR
- Haynes 214® alloy, sheet, 32 hours exposure at 980°C (1800°F)
- Multibase C6-150 Dow-Corning Class VI Elastomer
- SABIC Innovative Plastics LNP THERMOCOMP TH0815A PUR (Asia Pacific)
- A. Schulman SCHULADUR® A GF30 30% Glass Fiber Reinforced PBT
- Zircar Refractory Composites RS-A3 Refractory Sheet
- E-Polymers TEKAMID® H24M10 MF 10% Heat resistance Dimensional stability PA/ABS Alloy
- AK Steel ASTM A 1018, Grade 33 Hot Rolled Carbon Steel, Structural Steel (SS)
- ATI Allegheny Ludlum AL 50™ High Strength Stainless Steel, UNS S20910
- PolyOne Lubri-Tech™ AT-25GB/5T-2S Acetal-Copolymer, Glass Bead Filled, PTFE/Silicone Lubricated (discontinued
Copyright © lookpolymers.com All Rights Reserved