Polymer Resources PCSF-FRG20 Polycarbonate, 20% Glass Reinforced Structural Foam Grade
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled , Polycarbonate, Foam Grade, Glass Filled , Polycarbonate, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PCSF-FRG20 Polycarbonate, 20% Glass Reinforced Structural Foam Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycarbonate, 20% Glass Reinforced Structural Foam GradeFeatures: • Flame Retardant • Foamable • Self ExtinguishingProcess: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | ASTM D955 |
| Melt Flow | 4.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
4.0 - 10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D638 |
| Tensile Strength, Yield | 117 MPa | 17000 psi | ASTM D638 |
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| Flexural Modulus | 5.17 GPa | 750 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Temperature 22.8 °C |
1.50 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C | 300 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 285 °F | ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 1.59 mm |
V-2 @Thickness 0.0626 in |
|
| V-0 @Thickness 3.17 mm |
V-0 @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 293 - 316 °C | 560 - 600 °F | |
| Middle Barrel Temperature | 304 - 327 °C | 580 - 620 °F | |
| Front Barrel Temperature | 316 - 338 °C | 600 - 640 °F | |
| Melt Temperature | 302 - 329 °C | 575 - 625 °F | |
| Mold Temperature | 82.2 - 116 °C | 180 - 240 °F | |
| Drying Temperature | 118 - 124 °C | 245 - 255 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
Users viewing this material also viewed the following:
- Polymer Resources TP-FR-IM2-[color]-6 Polybutylene Terephthalate, Low Temperature Impact Modified, Flame Retardant
- Nitriflex N-8 NBR - Nitrile Rubber
- Kazanorgsintez 102-57 Low Density Polyethylene Composite, for Further Radiation Modification
- Fiberfil® J-60/10/FR Polypropylene Homopolymer, 10% Glass Reinforced, Flame Retardant
- LG Chemical LUPOY SC1004AU PC, High Impact
- Karina 08/240-FC-LMP Beige Color Concentrate for PVC
- Chevron Phillips MarFlex® D350 m-LLDPE Linear Low Density Polyethylene
- 3M 6035PC 12026 Polyurethane Foam Tape (15 lb./ft3 (239 kg/m3) Series)
- DSM Arnite® T06 202 PBT (European and Asian Grade)
- Wanhua Chemical Wanthane® WHT-6232 TPU Hot-Melt Adhesive
Copyright © lookpolymers.com All Rights Reserved