SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK3020 PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK3020 PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* Lexan_LGK3020 compound is a glass reinforced, flame retardant material.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Water Absorption | 0.13 % @Time 86400 sec |
0.13 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0025 cm/cm @Thickness 3.20 mm |
0.00050 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0015 - 0.0035 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0035 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 117 MPa | 17000 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Strength | 147 MPa | 21300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 6.57 GPa | 953 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 1.22 J/cm | 2.29 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
15.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 46.8 µm/m-°C @Temperature -30.0 - 30.0 °C |
26.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C @Thickness 6.40 mm |
295 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 17.7 kV/mm @Thickness 3.20 mm |
450 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP COLORCOMP J1000 PES (Europe-Africa-Middle East)
- Indium Corp. Indalloy® 51 Ga-In-Sn Alloy for Mercury Replacement
- Inno-Comp INNOPOL® CS 2-1000 Polypropylene Block-Copolymer
- H.C. Starck Amperit® 599.063 Agglomerated Sintered Molybdenum Carbide (Cr2O3)
- Sumitomo Bakelite North America 51-01 CAFR-P Mineral Filled Diallyl Phthalate
- Borealis Bormed™ BE860MO Polypropylene Copolymer for Healthcare Applications
- UBE UBEPOL B -B HIPS (Low-cis)
- A. Schulman ComAlloy Comtuf® 522 Polycarbonate/Styrenic Alloy
- Polystrand ThermoPro™ IE7021X ECR X-Ply Cross-Ply Polyethylene-Glass Composite
Copyright © lookpolymers.com All Rights Reserved