PolyOne Nymax™ X GMF 604 40 UV Black 148 rev 4 Polyamide 6 (Nylon 6)

Category	Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer	PolyOne Corporation
Trade Name	Nymax™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Nymax™ X GMF 604 40 UV Black 148 rev 4 Polyamide 6 (Nylon 6).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

The Nymax® GMF 600 Series of compounds are based upon nylon 6 resins and select combinations of glass fiber and mineral reinforcements offering a unique balance of physical property and part performance. These materials have been specifically formulated to offer ease of processing in most standard thermoplastic processing equipment.Molded Test Bars: Dry as MoldedInformation provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.48 g/cc	1.48 g/cc	ASTM D792
Density	1.49 g/cc	0.0538 lb/in³	ISO 1183
Water Absorption	1.0 %	1.0 %	24h/23C; ISO 62
	0.80 % @Thickness 3.18 mm	0.80 % @Thickness 0.125 in	@ 24 hrs; ASTM D570
Linear Mold Shrinkage	0.0020 - 0.0030 cm/cm	0.0020 - 0.0030 in/in	ISO 294-4
Linear Mold Shrinkage, Flow	0.0020 - 0.0040 cm/cm	0.0020 - 0.0040 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	117 MPa	17000 psi	Type I, 5.1 mm/min; ASTM D638
Tensile Strength, Yield	117 MPa	17000 psi	ISO 527-2
	121 MPa	17500 psi	Type I, 5.1 mm/min; ASTM D638
Elongation at Break	2.0 - 3.0 %	2.0 - 3.0 %	Type I, 5.1 mm/min; ASTM D638
	2.5 %	2.5 %	ISO 527-2
Tensile Modulus	8.27 GPa	1200 ksi	ASTM D638
	8.50 GPa	1230 ksi	ISO 527-2
Flexural Strength	179 MPa	26000 psi	ASTM D790
	190 MPa	27600 psi	ISO 178
Flexural Modulus	7.58 GPa	1100 ksi	ASTM D790
	8.40 GPa	1220 ksi	ISO 178
Izod Impact, Notched	0.690 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	1.29 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A
Izod Impact, Notched (ISO)	13.0 kJ/m²	6.19 ft-lb/in²	ISO 180

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	195 °C	383 °F	Annealed; ISO 75-2/A

Processing Properties	Metric	English
Mold Temperature	60.0 - 107 °C	140 - 225 °F
Drying Temperature	82.2 °C	180 °F
Dry Time	4.00 hour	4.00 hour

Descriptive Properties	Value	Comments
Additive	Heat Stabilizer
	UV Stabilizer
Appearance	Black
Automotive Specifications	CHRYSLER MS-DB41 CPN3916
Features	General Purpose
	Heat Stabilized
Filler / Reinforcement	GlassMineral, 40% Filler by Weight
Forms	Pellets
Generic Material	Nylon 6
Generic Name	Polyamide 6 (Nylon 6)
Processing Method	Injection Molding
Regional Availability	North America
	South America
Uses	Automotive Applications
	Construction Applications
	Consumer Applications
	General Purpose
	Industrial Applications