Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 93.0 MPa | 13500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycoloy® C4220 PC+ABS PC+ABS Blend with 20% Glass Reinforce. High heat resistance; Excellent balance strength/rigidity; Good impact/appearance. |
|||
Tensile Strength at Break | 93.1 MPa | 13500 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Edgetek® NY-20GF/10GB/000 Polyamide 6 (Nylon 6) Information provided by PolyOne |
|||
Tensile Strength at Break | 93.0 MPa | 13500 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DCP32 PC LNP* Lubricomp* DCP32 is a compound based on Polycarbonate resin containing 15% PTFE/Silicone, 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubrica.. |
|||
Tensile Strength at Break | 93.2 MPa @Thickness 3.20 mm |
13500 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
LG Chemical Lupox® GP2156FL PBT+GF15% Description: Injection Molding, PBT+GF15%, Flame Retardant Application: IT/OA, E&E (CRT Socket)CAS No. 68928-70-1, 71342-77-3, 65997-17-3, 24968-12-5, 25038-59-9 and 1309-64-4Information provided by.. |
|||
Tensile Strength at Break | 93.0 MPa | 13500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1520A PC (Asia Pacific) 20% glass reinforced/15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances. |
|||
Tensile Strength at Break | 93.0 MPa | 13500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON DEL329E PC (Asia Pacific) LNP* Stat-kon* DEL329E is a compound based on Polycarbonate resin containing PTFE, Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, .. |
|||
Tensile Strength at Break | 93.0 MPa | 13500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® DR48 PBT 17% glass reinforced, flame retardant grade UL-94 rated V-0/5VA. |
|||
Tensile Strength at Break | 93.0 MPa | 13500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® DR51 PBT (Asia Pacific) 15% GR polyester, excellent mechanical, thermal and electrical performance. Non-flame retardant. Spotlights, appliance housings, handles, connectors |
|||
Tensile Strength at Break | 93.0 MPa | 13500 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP DF0029P PC LNP THERMOCOMP* DF0029P is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added features of this material include: Exceptional Processing. Flame Retardant. |
|||
Tensile Strength at Break | 93.0 MPa | 13500 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOTUF VFK33S PA 66 LNP THERMOTUF* VFK33S is a compound based on Nylon resin containing Glass Fiber, Mineral. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 93.1 MPa | 13500 psi | ASTM D638 |
A. Schulman COMTUF® 462 Glass/Fiber Mineral Reinforced, Impact Modified PET Alloy Information provided by A. Schulman. |
|||
Tensile Strength at Break | 93.1 MPa | 13500 psi | ASTM D638 |
A. Schulman ComAlloy® E-12421 Reinforced High Flow Polyamide Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength at Break | 93.1 MPa | 13500 psi | DIN EN ISO 527 |
Wolf Kunststoff ZEDEX® ZX-750V5KF 055 Polymer Alloy. Fiber Reinforced Main Characteristics: Stiff; High elongation and yield stress; Low thermal expansion; Impact resistantApplications: Textile Machinery; Compressors; Hinges; Handling; Machine Tools; Automitve Technol.. |
|||
Tensile Strength at Break | 93.1 MPa | 13500 psi | ASTM D638 |
A. Schulman ComAlloy® E-12421 Reinforced High Flow Polyamide Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength at Break | 93.1 MPa | 13500 psi | ASTM D638 |
A. Schulman COMTUF® 462 Glass/Fiber Mineral Reinforced, Impact Modified PET Alloy Information provided by A. Schulman. |
|||
Tensile Strength at Break | 93.1 MPa | 13500 psi | ASTM D638 |
A. Schulman ComAlloy® E-12421 Reinforced High Flow Polyamide Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength at Break | 93.1 MPa | 13500 psi | ASTM D638 |
A. Schulman COMTUF® 462 Glass/Fiber Mineral Reinforced, Impact Modified PET Alloy Information provided by A. Schulman. |
|||
Tensile Strength at Break | 93.1 MPa | 13500 psi | ASTM D638 |
A. Schulman COMTUF® 462 Glass/Fiber Mineral Reinforced, Impact Modified PET Alloy Information provided by A. Schulman. |
|||
Tensile Strength at Break | 93.0 MPa | 13500 psi | 5 mm/min; ISO 527 |
Eurostar Staramide PFB42ES PA6, Glass Fiber/Bead Filled, Injection Molded Starflam PFB42ES is a Glass Bead and Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength at Break | 93.0 MPa | 13500 psi | 5 mm/min; ISO 527 |
Eurostar Staramide PFB42EU PA6, Glass Fiber/Bead Filled, Injection Molded Starflam PFB42EU is an UV Stabilized, Glass Bead and Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength at Break | 93.1 MPa | 13500 psi | ASTM D638 |
Entec Hylox® 9015 PBT, 15% Glass Reinforced Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Ente.. |
|||
Tensile Strength at Break | 93.0 MPa | 13500 psi | 0.2 in/min; ASTM Test |
BASF Ultradur B 4300 G3 15% Glass Filled PBT Ultradur B 4300 G3 is an easy flowing injection molding PBT with 15% glass fiber reinforcement for rigid, tough, and dimensionally stable parts. |
|||
Tensile Strength at Break | 93.0 MPa | 13500 psi | 0.2 in/min; ASTM Test |
BASF Ultramid® TG3S BK-104 15% Glass Filled PA6 (Dry) Ultramid TG3S BK-104 is a 15% glass reinforced, heat stabilized, impact modified PA6 injection molding compound developed for applications requiring improved toughness in combination with a balance .. |