SABIC Innovative Plastics LNP THERMOTUF VFK33S PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Thermotuf
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOTUF VFK33S PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP THERMOTUF* VFK33S is a compound based on Nylon resin containing Glass Fiber, Mineral. Added features of this material include: Heat Stabilized.
Physical Properties Metric English Comments
Density 1.325 g/cc
0.04787 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0030 cm/cm

@Time 86400 sec
 0.0030 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 93.0 MPa
13500 psi
ASTM D638
Elongation at Break 3.2 %
3.2 %
ASTM D638
Tensile Modulus 6.27 GPa
909 ksi
50 mm/min; ASTM D638
Flexural Strength 147 MPa
21300 psi
ASTM D790
Flexural Modulus 5.28 GPa
766 ksi
ASTM D790
Izod Impact, Notched 1.09 J/cm
2.04 ft-lb/in
ASTM D256
Izod Impact, Unnotched 7.81 J/cm
14.6 ft-lb/in
ASTM D4812
Dart Drop, Total Energy 13.0 J
9.59 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 29.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
 16.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 78.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 43.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 256 °C

@Thickness 3.20 mm
 493 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 239 °C

@Thickness 3.20 mm
 462 °F

@Thickness 0.126 in
 unannealed; ASTM D648