SABIC Innovative Plastics Cycoloy® C4220 PC+ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycoloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycoloy® C4220 PC+ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PC+ABS Blend with 20% Glass Reinforce. High heat resistance; Excellent balance strength/rigidity; Good impact/appearance.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D792 |
| Melt Flow | 16 g/10 min @Load 5.00 kg, Temperature 260 °C |
16 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 93.0 MPa | 13500 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 92.0 MPa | 13300 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 6.41 GPa | 930 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 146 MPa | 21200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 5.79 GPa | 840 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| 0.640 J/cm @Temperature -30.0 °C |
1.20 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 4.53 J/cm | 8.49 ft-lb/in | ASTM D4812 |
| 4.80 J/cm @Temperature -30.0 °C |
8.99 ft-lb/in @Temperature -22.0 °F |
ASTM D4812 | |
| Dart Drop, Total Energy | 19.0 J @Temperature -30.0 °C |
14.0 ft-lb @Temperature -22.0 °F |
ASTM D3763 |
| 21.0 J @Temperature 23.0 °C |
15.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C @Thickness 3.20 mm |
264 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 132 °C @Thickness 6.40 mm |
270 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Chevron Phillips Vytek™ V208A Enhanced LLDPE Blown Film Resin (discontinued **)
- DSM Somos® WaterClear® 10110 Epoxy Resin for Stereolithography (discontinued **)
- Haynes 25 alloy, room temperature sheet after 100 hours of 760°C exposure
- Sinotek Materials ZSLZ83 Middle Carbon Graphite
- Unipetrol PP MONSTEN® MA 611 Polypropylene Impact Copolymer
- Eagle Brass 770 Nickel Silver 18%, 3/4 Hard
- ConocoPhillips Hydroclear® El Mar® 30 Ashless Supreme
- Adell BT-33 Nylon 6, 15% Glass Reinforced; Impact Modified
- BASF Neopolen® P 9230 K 0.05 g/cc Core density; Expanded Polypropylene (Europe)
- Bhansali Engineering Abstron IMG1130 Glass Reinforced Grade
Copyright © lookpolymers.com All Rights Reserved