SABIC Innovative Plastics LNP THERMOCOMP DF0029P PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF0029P PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* DF0029P is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added features of this material include: Exceptional Processing. Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| 1.318 g/cc | 0.04762 lb/in³ | ASTM D792 | |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0042 cm/cm @Time 86400 sec |
0.0042 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0048 cm/cm @Time 86400 sec |
0.0048 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 92.0 MPa | 13300 psi | ASTM D638 |
| 93.0 MPa | 13500 psi | ISO 527 | |
| Elongation at Break | 3.8 % | 3.8 % | ASTM D638 |
| 3.8 % | 3.8 % | ISO 527 | |
| Tensile Modulus | 4.61 GPa | 669 ksi | 50 mm/min; ASTM D638 |
| 4.80 GPa | 696 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 155 MPa | 22500 psi | ASTM D790 |
| 158 MPa | 22900 psi | ISO 178 | |
| Flexural Modulus | 4.68 GPa | 679 ksi | ASTM D790 |
| 5.00 GPa | 725 ksi | ISO 178 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.05 J/cm | 7.59 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² | 15.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J | 3.69 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 134 °C | 273 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 136 °C @Thickness 3.20 mm |
277 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 0.640 mm |
V-0 @Thickness 0.0252 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Palm Labs Adhesives TURBO SEAL SERIES 85 WHITE STAINLESS STEEL THREAD SEALANT
- Resinlab® CYNERGY CA6501 Adhesive
- ExxonMobil Mobil Turbo 24
- Wall Colmonoy COLMONOY® 83 PTA - Nickel-Chromium-Boron Matrix Alloy With Tungsten Carbide
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 0.35 PHR Caytur 4
- China Tungsten ST1260 PM Antifriction Parts
- Eurostar Starflam PF0057E PA6, 25% Glass Filled, Injection Molded
- BASF Nypel® 6015G HS BK 15% Glass Filled PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved