Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 86.0 MPa | 12500 psi | ISO.527 DIN.53455 |
Omnia Plastica Akulon® PA 66.6 Akulon GX - Dry Copolymer of nylon with excellent mechanical features, it combines the good impact resistances of PA6 as well as the higher stiffness of PA66. For this reason it machines very well on automatic tool.. |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycoloy® MC5215 PC+ABS |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® MC5215 PC+ABS |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® MC5215 PC+ABS (Asia Pacific) |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | |
Radici Radilon® S ERV3808K (cond.) Nylon 6 Radilon® S is a range of polyamide 6 (PA6) products obtained through the polymerization of caprolactam and used for injection, extrusion and blow-molding.Information provided by Radici group. |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP DFL36G PC LNP* Lubricomp* DFL36G is a compound based on Polycarbonate resin containing 30% Mixed Glass, 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 86.0 MPa @Temperature 23.0 °C |
12500 psi @Temperature 73.4 °F |
DAM; ISO 527 |
DuPont Performance Polymers Minlon® 11C40 BKB086 Nylon 66
(Unverified Data**) Minlon® 11C40 BKB086 is a 40% mineral reinforced, heat stabilized, black polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP LX82803 PEEK (Europe-Africa-Middle East) LNP* LUBRICOMP* LX82803 is a compound based on Polyetheretherketone resin containing Proprietary Lubricant. Added features include : Internally Lubricated. |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP SX93441D PA12 LNP* Lubricomp* SX93441D is a compound based on Nylon 12 containing Proprietary Fillers. Characteristics of this grade are: Internally Lubricated. |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Lubricomp SX93441D PA6.12 LNP* Lubricomp* SX93441D is a compound based on Nylon 6/12 containing Proprietary Fillers. Characteristics of this grade are: Internally Lubricated.This data was supplied by SABIC-IP for the Ameri.. |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Ultem 2313 PEI 30% Milled glass filled, enhanced flow Polyetherimide (Tg 217C) with enhanced electroplatability. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region... |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRILOY UA200A PPA LNP LUBRILOY* UA200A is a compound based on Polyphthalamide resin containing Aramid Fiber, Proprietary Lubricant. Added feature of this material is: Wear Resistant. |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRILOY UA200A PPA (Asia Pacific) LNP LUBRILOY* UA200A is a compound based on Polyphthalamide resin containing Aramid Fiber, Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON Noryl_HMC202M PPE+HIPS (Europe-Africa-Middle East) DATA ON BK1005 ONLY. |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp DFZ42P PC LNP* Thermocomp* DFZ42P is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Exceptional Processing.This data was supplied by SABIC-IP for the.. |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp GF003 PSU LNP THERMOCOMP* GF003 is a compound based on Polysulfone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp GF003 PSU LNP THERMOCOMP* GF003 is a compound based on Polysulfone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP KF002 Acetal Copolymer LNP THERMOCOMP* KF002 is a compound based on Acetal Copolymer resin containing 10% Glass Fiber. |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP KX97390 Acetal Copolymer LNP THERMOCOMP* KX97390 is a compound based on Acetal Copolymer resin containing Glass Fiber. Added features of this material include: Chemically Coupled. |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP MF008S PP LNP THERMOCOMP* MF008S is a compound based on Polypropylene resin containing 30% Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized. |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP SF004S PA12 LNP* Thermocomp* SF004S is a compound based on Nylon 12 containing 20% glass fiber. Added features include: Heat Stabilized, Healthcare |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | ASTM D638 |
Sumitomo Bakelite North America E 8940SG Electrical Encapsulation Grade Epoxy Mineral reinforced epoxy molding compound formulated for the encapsulation of electronic devices requiring high quality, exceptional reliability, and outstanding moldability. USES: Passive electron.. |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DFD03 PC LNP* STAT-KON* DFD03 is a compound based on Polycarbonate containing 15% Glass Fiber. Added feature of this grade is: Impact Modified. |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP KF002XXP Acetal Copoly LNP* Thermocomp* KF002XXP is a compound based on Acetal Copolymer resin containing 10% Glass Fiber. Added features of this material include: Chemically Coupled. |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | ASTM D638 |
Sumitomo Bakelite Durez® 32245 Phenolic, Injection Grade Durez 32245 Black Phenolic is a two-stage glass fiber and mineral filled special purpose molding compound. It is especially designed for applications requiring high strength and dimensional stabilit.. |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Minlon® 11C40 BKB086 Nylon 66
(Unverified Data**) 40% Mineral Reinforced Polyamide 66 Minlon 11C40 BKB086 is a 40% mineral reinforced heat stabilized black polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers.. |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP DFL36G PC (Asia Pacific) LNP* Lubricomp* DFL36G is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Milled Glass. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DFL44 PC (Europe-Africa-Middle East) LNP* Lubricomp* DFL44 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. |