SABIC Innovative Plastics LNP THERMOCOMP MF008S PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP MF008S PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* MF008S is a compound based on Polypropylene resin containing 30% Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 86.0 MPa | 12500 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
| Flexural Modulus | 7.44 GPa | 1080 ksi | ASTM D790 |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.87 J/cm | 11.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Samsung Cheil Industries Starex® VG-4910 ABS, Glass Filled FR
- Tipco Tipcolene® PPH-OIT - Unfilled Polypropylene Homopolymer Compound with Copper Inhibitor (Metal Deactivator)
- American Elements Bismuth Oxide Nanopowder
- Eagle Brass 521 Phosphor Bronzes 8% C, Annealed
- Dow Corning SYL-OFF® 297 ANCHORAGE ADDITIVE
- Aleris Hokotol Aluminum Alloy, 200 mm Thickness
- Bulk Molding Compounds BMC 665 Mineral filled, 20% glass reinforced polyester molding compound
- Loxim 830 01 HB Polypropylene Compound, Flame Retardant
- Hydrogenated Nitrile Rubber (HNBR)
Copyright © lookpolymers.com All Rights Reserved