SABIC Innovative Plastics LNP THERMOCOMP SF004S PA12
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP SF004S PA12.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* SF004S is a compound based on Nylon 12 containing 20% glass fiber. Added features include: Heat Stabilized, Healthcare
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D792 |
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.140 % | 0.140 % | 50% RH, 24 hrs; ASTM D570 |
| 0.190 % | 0.190 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
| 86.0 MPa | 12500 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 5.21 GPa | 756 ksi | 1 mm/min; ISO 527 |
| 5.40 GPa | 783 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 104 MPa | 15100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 116 MPa | 16800 psi | ISO 178 | |
| Flexural Yield Strength | 131 MPa | 19000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.45 GPa | 645 ksi | 2 mm/min; ISO 178 |
| 4.60 GPa | 667 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.870 J/cm | 1.63 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.93 J/cm | 11.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J @Temperature 23.0 °C |
8.11 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 39.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
21.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 10.6 µm/m-°C @Temperature -30.0 - 30.0 °C |
5.89 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 176 °C @Thickness 3.20 mm |
349 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 166 °C @Thickness 3.20 mm |
331 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Radici Raditer® B N 100 T Polybutylene Terephthalate
- Huntsman Araldite 98-311 Bisphenol F Epoxy Resin
- SABIC Innovative Plastics LNP Thermocomp LF003E PEEK (Asia Pacific)
- Teknor Apex ELEXAR® EL 8451 Thermoplastic Elastomer
- Wellman Wellpet® GF100-N1 30% Glass Fiber Reinforced, Natural PET
- Cossa Polimeri ESTAPROP H 2560 C Polypropylene, 30% Mineral Filled
- ExxonMobil Mobil Rarus 1026 SHC 1000 Series
- Chosun Refractories SR Blast Furnace Runner Refractory
- Fainplast Compounds GS 69/PL Flexible PVC, Injection Molding for Footwear
- Arkema Group Lucalor® RY 123 CPVC, Plumbing Grade
Copyright © lookpolymers.com All Rights Reserved