SABIC Innovative Plastics LNP Thermocomp GF003 PSU
| Category | Polymer , Thermoplastic , Polysulfone (PSU) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp GF003 PSU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* GF003 is a compound based on Polysulfone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ASTM D 792 |
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D 792 |
| 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.34 % | 0.34 % | 23°C / 50% RH; ISO 62 |
| 0.21 % @Time 86400 sec |
0.21 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 86.0 MPa | 12500 psi | Type I, 5 mm/min; ASTM D 638 |
| 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.1 % | 3.1 % | Type I, 5 mm/min; ASTM D 638 |
| 3.1 % | 3.1 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.8 % | 2.8 % | 5 mm/min; ISO 527 |
| 2.9 % | 2.9 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 5.42 GPa | 786 ksi | 1 mm/min; ISO 527 |
| 5.49 GPa | 796 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 146 MPa | 21200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 4.71 GPa | 683 ksi | 2 mm/min; ISO 178 |
| 4.72 GPa | 685 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.450 J/cm @Temperature 23.0 °C |
0.843 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 5.50 J/cm @Temperature 23.0 °C |
10.3 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 37.0 kJ/m² @Temperature 23.0 °C |
17.6 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| 14.0 J @Temperature 23.0 °C |
10.3 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 31.8 µm/m-°C @Temperature -30.0 - 30.0 °C |
17.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 55.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
30.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 185 °C | 365 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 184 °C @Thickness 3.20 mm |
363 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 179 °C | 354 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 178 °C @Thickness 3.20 mm |
352 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- PolyOne Lubri-Tech™ AT-000/8T Acetal-Copolymer, PTFE Lubricated (discontinued **)
- Lord Adhesives Aeroglaze® K3425 Sandable Primer/Surfacer
- Lucas-Milhaupt Silvaloy® A35 Brazing Alloy
- SSAB Tunnplat Docol® DC04 (Fe P04) Deep-drawing Steel
- Techmer ES Electrablend® PA6 GF20 20% Glass Filled
- Teknor Apex Sinpolene MBW008LE Low Density Polyethylene
- 3M 25X126 Protective UV Tape
- 3M 4104 Single-Coated Foam Tape
Copyright © lookpolymers.com All Rights Reserved