SABIC Innovative Plastics LNP LUBRICOMP LX82803 PEEK (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP LX82803 PEEK (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* LX82803 is a compound based on Polyetheretherketone resin containing Proprietary Lubricant. Added features include : Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm | 0.0090 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 87.0 MPa | 12600 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 8.3 % | 8.3 % | Flexural Strain, break, 2 mm/min; ISO 178 |
| Elongation at Yield | 4.4 % | 4.4 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 4.60 GPa | 667 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 151 MPa | 21900 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.90 GPa | 711 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 39.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
21.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 49.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
27.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 207 °C | 405 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 153 °C | 307 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® IP1000 PC+ABS
- Quadrant EPP TIVAR® 88-2 ESD Black, Premium Lubricant Filled, Lower COF, Electro Static Dissipative Lining Material (ASTM Product Data Sheet)
- Zyvex Performance Materials Arovex™ HT 250 Nano-Engineered Composite Prepreg System
- CP-Polymer-Technik Wellamid® 6000/42 Nylon 6, Polymer Modified, Conditioned
- Daikin NEOFLON EPW-1606BL ETFE Liquid Primer, Blue
- Bulk Molding Compounds BMC T44-15613 High Strength Mineral Filled Molding Compound
- Nitrile Rubber (NBR, Acrylonitrile-Butadiene Rubber)
- BP Amoco Acctuf® 3432 Impact Copolymer Polypropylene (discontinued **)
- LG Chemical HG-174 ABS, High Gloss, Super High Flow
Copyright © lookpolymers.com All Rights Reserved