SABIC Innovative Plastics Cycoloy® MC5215 PC+ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycoloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycoloy® MC5215 PC+ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| Water Absorption at Saturation | 0.15 % | 0.15 % | ISO 62 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 260 °C |
20 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Melt Index of Compound | 17 g/10 min @Load 2.16 kg, Temperature 260 °C |
17 g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 86.0 MPa | 12500 psi | Type I, 5 mm/min; ASTM D638 |
| 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 5.77 GPa | 837 ksi | 5 mm/min; ASTM D638 |
| 5.91 GPa | 857 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 134 MPa | 19400 psi | 2 mm/min; ISO 178 |
| 135 MPa | 19600 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 4.97 GPa | 721 ksi | 2 mm/min; ISO 178 |
| 5.15 GPa | 747 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.700 J/cm | 1.31 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched (ISO) | 32.0 kJ/m² | 15.2 ft-lb/in² | 80*10*3; ISO 180/1U |
| 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C @Thickness 3.20 mm |
203 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 100 °C | 212 °F | Rate B/120; ISO 306 |
| Flammability, UL94 | V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
UL 94 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL1132 PC Copolymer
- Premix Premi-Glas® 8102-20 Glass Reinforced Polyester BMC (discontinued **)
- Mearthane Durethaneâ„¢ S DS-545D Solid Polyurethane Elastomer
- Kuraray HYBRAR® HD2 Thermoplastic Rubber-HDPE Blend
- Momentive Performance Materials IS808 One-Component, Paste Consistency Silicone Rubber Adhesive Sealant, Translucent
- Kraton® D1126 P (SIS) Radial Copolymer
- SABIC Innovative Plastics SABIC PPCOMPOUND 55T1040 PP
- Eastman DuraStar MN610 Polymer, Natural
- ExxonMobil ESCOREZ™ 5320 Petroleum Hydrocarbon Resin
- Clariant 6004G8-HSL BK UV Black Nylon 6, 8% Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved