SABIC Innovative Plastics LNP THERMOCOMP KF002 Acetal Copolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 10% Glass Fiber Reinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP KF002 Acetal Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* KF002 is a compound based on Acetal Copolymer resin containing 10% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| 1.454 g/cc | 0.05253 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.190 % | 0.190 % | 50% RH, 24 hrs; ASTM D570 |
| 0.350 % | 0.350 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0116 cm/cm @Time 86400 sec |
0.0116 in/in @Time 24.0 hour |
ISO 294 |
| 0.012 cm/cm @Time 86400 sec |
0.012 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0129 cm/cm @Time 86400 sec |
0.0129 in/in @Time 24.0 hour |
ISO 294 |
| 0.013 cm/cm @Time 86400 sec |
0.013 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ASTM D638 |
| 86.0 MPa | 12500 psi | ISO 527 | |
| Elongation at Break | 3.2 % | 3.2 % | ASTM D638 |
| 3.4 % | 3.4 % | ISO 527 | |
| Tensile Modulus | 4.75 GPa | 689 ksi | 50 mm/min; ASTM D638 |
| 5.40 GPa | 783 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 129 MPa | 18700 psi | ASTM D790 |
| 137 MPa | 19900 psi | ISO 178 | |
| Flexural Modulus | 4.61 GPa | 669 ksi | ASTM D790 |
| 5.40 GPa | 783 ksi | ISO 178 | |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.48 J/cm | 8.39 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² | 15.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 164 °C @Thickness 3.20 mm |
327 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 161 °C | 322 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 161 °C @Thickness 3.20 mm |
322 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Dynalloy™ 8900-60 Thermoplastic Elastomer (TPE)
- Mallard Creek Polymers ROVENE® 4002 SBR Latex
- LG Chemical LUPOL HF-3308 High Flow Polypropylene, 30% Mineral Fillers
- Techmer ES Elastoblend® PA6 IM X
- Techmer ES Electrablend® TPX-HTN-01045 A 40% Carbon Filled
- Ensinger Tecapeek® XP-108 Compression Molded PEEK Compound, 20% PTFE Filled
- 3M Fluorinert™ FC-72 Electronic Liquid
- Zotefoams Plastazote® LD15 Low Density Polyethylene Foam
Copyright © lookpolymers.com All Rights Reserved