SABIC Innovative Plastics LNP STAT-KON Noryl_HMC202M PPE+HIPS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON Noryl_HMC202M PPE+HIPS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DATA ON BK1005 ONLY.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 7.6 g/10 min @Load 5.00 kg, Temperature 300 °C |
7.6 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 |
| 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 86.0 MPa | 12500 psi | 5 mm/min; ISO 527 |
| 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 4.1 % | 4.1 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 4.1 % | 4.1 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 7.58 GPa | 1100 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 135 MPa | 19600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 145 MPa | 21000 psi | 2 mm/min; ISO 178 | |
| Flexural Yield Strength | 145 MPa | 21000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.89 GPa | 999 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 7.15 GPa | 1040 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.67 J/cm | 5.00 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Dart Drop, Total Energy | 9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 13.0 µm/m-°C @Temperature 23.0 - 150 °C |
7.22 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| 61.2 µm/m-°C @Temperature -30.0 - 30.0 °C |
34.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 | |
| CTE, linear, Transverse to Flow | 57.0 µm/m-°C @Temperature 23.0 - 150 °C |
31.7 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| 158 µm/m-°C @Temperature -30.0 - 30.0 °C |
87.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C @Thickness 3.20 mm |
351 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 181 °C @Thickness 6.40 mm |
358 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 171 °C @Thickness 3.20 mm |
340 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 173 °C @Thickness 6.40 mm |
343 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 180 °C | 356 °F | Rate B/50; ASTM D1525 |
| 180 °C | 356 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | V-1 @Thickness 1.49 mm |
V-1 @Thickness 0.0587 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10000 ohm | 10000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 80-8470 Polyacetal-copolymer, unreinforced
- SABIC Innovative Plastics Xenoy® X5500EX PBT+PC (Asia Pacific)
- Star Plastics ABSFR2 Molding Grade ABS
- Styrolution NAS® 36 UV Stabilized Acrylic Copolymer
- Solvay SUPRAGIL® GN 4-4’ Dihydroxydiphenyl Sulphonate Condensate Sodium Salt
- Westlake Plastics Pomalux® 25% GF Acetal Copolymer 25% Glass Filled
- ELASTO UK Dryflex® 402901S SBS Based Material, 90A Hardness, Black
- Ensinger TECANYL™ MT CF30 Autoclavable Polymer
- Diamond Polymers ASA S150
- Eurotec® Tecomid® NA40 GR40 NL HS PA6.6, 40% glass fiber reinforced, heat stabilized, natural
Copyright © lookpolymers.com All Rights Reserved