Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | <= 32.0 MPa | <= 4640 psi | ISO/R527 |
Polykemi AB POLYfill PPH T2020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS (Europe-Africa-Middle East) LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | <= 32.0 MPa | <= 4640 psi | ISO/R527 |
Polykemi AB POLYfill PPH T5020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS LNP LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing 10% PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS (Europe-Africa-Middle East) LNP* LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
Braskem BS 002J HDPE Blow Molding Polyethylene
(discontinued **) Applications: Bottles up to 60 liters with high ESCR; bottles for surface-active agents. Information provided by Braskem |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO R 527 |
Fainplast Compounds RE 325/2 Rigid PVC, Extrusion Building profiles |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO R 527 |
Fainplast Compounds RH 207/OP Rigid PVC, Antishock Extrusion Medium antishock satined profiles |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO 37 |
Huntsman AVALON® 90 AB Thermoplastic Polyurethane Performance Features: AVALON® injection molding products are trusted worldwide to deliver:Outstanding flex performanceExcellent slip resistancePerfect surface definitionTransparency and transluce.. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | DIN 53504 |
Huntsman IROGRAN® A 80 P 5039 TPU-Polyether Excellent resistance to hydrolysis and microbial attack. Suggested for injection molding and extrusion.Information provided by Huntsman |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
LG Chemical HI835HS PMMA, Impact Resistant Grade Molding granule designed for greater impact strength combined with the outstanding properties of conventional acrylic materialsFeatures: Excellent transparency and eleganceWeather resistance and che.. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
LG Chemical HI855HS PMMA, Impact Resistant Grade Molding granule designed for greater impact strength combined with the outstanding properties of conventional acrylic materialsFeatures: Excellent transparency and eleganceWeather resistance and che.. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO 37 |
Huntsman AVALON® 90 ABR Thermoplastic Polyurethane Introduction: AVALON 90 ABR is a high performance polyester based thermoplastic polyurethane for injection molding. AVALON 90 ABR is part of the AVALON Performance Range and offers a premium soling .. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON FD000 PE LNP* STAT-KON* FD000 is an unfilled Polyethylene. Added feature of this grade is: Electrically Conductive. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON FX98501 PE LNP* STAT-KON* FX98501 is a compound based on Polyethylene resin containing Proprietary Fillers. Added feature of this material is: Electrically Conductive. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Stat-loy K3000 Acetal Copoly (Asia Pacific) LNP* Stat-loy* K3000 is a compound based on Acetal Copolymer resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Asia Pacific .. |
|||
Tensile Strength at Break | >= 32.0 MPa | >= 4640 psi | ISO R 527 |
Stir SpA Giesse RSA/12 (PVC) Application: Blow molding very high shock resistanceInformation provided by STIR SpA |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP AB002 ABS LNP* THERMOCOMP* AB002 is a compound based on ABS resin containing 10% Glass Bead. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO 527 |
Total 3802 Blue MDPE pipe, injection molding FINATHENE® 3802 Blue is a polyethylene copolymer based on C6 hexene as co-monomer and is produced by a continuous low pressure slurry polymerization process. FINATHENE® 3802 Blue is a blue polyeth.. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D 638 |
Cossa Polimeri ESTADIENE 3008 MT Acrylonitrile Butadiene Styrene ABS with very high impact resistanceHigh impact resistance at low temperature, medium heat resistance, good processabilityInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO 527-1/-2 |
DuPont Performance Polymers Hytrel® HTR8139BK Polyester Elastomer TPC-ET
(Unverified Data**) 44 Shore D Lubricated High Viscosity Polyester Elastomer Developed for Blow Molding Hytrel HTR8139BK is designed for blow molding or processing techniques requiring high melt viscosity. It has nomin.. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | Conditioned 15 days at 23°C - 50% RH; ASTM D638 |
Arkema Group Pebax® 2533 SA 01 Polyether Block Amide (PEBA) Polyether block amide PEBAX® 2533 SA 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This SA grade is specially designed to food uses.Information provided by Arkema .. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0334G10M20CL Glass/Mineral Reinforced Coupled |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | Conditioned; ISO R 527 |
Addiplast Addilene H 490 M10S Flame Retardant Polypropylene Flame retardant, mineral filled, with halogensInformation provided by Addiplast. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | Conditioned; ISO R 527 |
Addiplast Addilene H 490 S Flame Retardant Polypropylene Flame retardant, unreinforced, with halogensInformation provided by Addiplast. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | |
AorTech Biomaterials ECSil™ 75A Biomedical Carbonate Silicone Pellets Elast-Eon™ Carbonate Silicone (ECSil™) is a family of next generation biomedical polymers. ECSil™ is finding strong interest in cardiac pacing leads, orthopaedics, spinal discs, and generally an.. |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | DIN EN ISO 527-3 |
3M Dyneon™ TF 2053Z PTFE Fine Powder Dyneon™ TF 2053 Z PTFE is an ideal grade for extrusion of tubing and cables requiring only moderately high reduction ratio.Product Features:Processable by standard paste extrusion methods Good over.. |
|||
Tensile Strength at Break | <= 32.0 MPa | <= 4640 psi | ISO/R527 |
Polykemi AB POLYfill PPH T8020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO R 527 |
Fainplast Compounds RE 230/D Rigid PVC, Extrusion Electric channels |