Huntsman IROGRAN® A 80 P 5039 TPU-Polyether
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 80 P 5039 TPU-Polyether.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent resistance to hydrolysis and microbial attack. Suggested for injection molding and extrusion.Information provided by Huntsman
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D995 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 80 | 80 | ASTM D2240 |
| Hardness, Shore D | 29 | 29 | ASTM D2240 |
| Tensile Strength at Break | 32.0 MPa | 4640 psi | DIN 53504 |
| Elongation at Break | 760 % | 760 % | ASTM D412 |
| 100% Modulus | 0.00460 GPa | 0.667 ksi | DIN 53504 |
| 300% Modulus | 0.00870 GPa | 1.26 ksi | DIN 53504 |
| Rebound | 47 % | 47 % | Bayshore; ASTM D2632 |
| Tear Strength | 84.1 kN/m | 480 pli | ASTM D624 |
| Abrasion | 30 | 30 | [mm<sup>3</sup>]; ISO 4649 |
| Compression Set | 23 % @Temperature 23.0 °C, Time 252000 sec |
23 % @Temperature 73.4 °F, Time 70.0 hour |
ASTM D395 |
| 43 % @Temperature 70.0 °C, Time 86400 sec |
43 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 145 - 155 °C | 293 - 311 °F | Huntsman/TMA |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not reported |
Users viewing this material also viewed the following:
- Polykemi AB POLYabs N30 ABS
- PolyOne Geon™ 81520 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Haynes 556® alloy, bar, after 1000 hours at 870°C (1600°F)
- Solvay Specialty Polymers Amodel® A-1933 HSL Polyphthalamide (PPA), 33% Glass Fiber
- Stir SpA AF 93 CZ BL (PVC)
- Polyram Polytron P50N01 Homopolymer Polypropylene, Chemically Coupled 50% Long Glass Fiber
- A. Schulman FORMION™ FI 105 Non-Reinforced, Injection Molding Grade Sodium Ionomer
- Covestro Makrolon® 6487 Polycarbonate, Flame Retardant Grade
- Braskem EB 861 LDPE Blown Film Extrusion Polyethylene
- NOVA Chemicals Sclair® 2508-UV13 MDPE Injection Molding Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved