DuPont Performance Polymers Hytrel® HTR8139BK Polyester Elastomer TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® HTR8139BK Polyester Elastomer TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
44 Shore D Lubricated High Viscosity Polyester Elastomer Developed for Blow Molding Hytrel HTR8139BK is designed for blow molding or processing techniques requiring high melt viscosity. It has nominal hardness of 44D is pigmented black with fine particInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 0.960 g/cc
0.0347 lb/in³
1.15 g/cc
0.0415 lb/in³
ISO 1183
Water Absorption 0.70 %

@Thickness 2.00 mm
 0.70 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
 0.200 %

@Thickness 0.0787 in
 Sim. to ISO 62
Water Absorption at Saturation 0.70 %
0.70 %
Immersion 24h; ASTM D570
Linear Mold Shrinkage, Flow 0.016 cm/cm
0.016 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.014 cm/cm
0.014 in/in
ISO 294-4 2577
Melt Flow 1.9 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 1.9 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 cm³/10min; ISO 1133
2.1 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 2.1 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 40
40
15s; ISO 868
<= 44
<= 44
ISO 868
Tensile Strength at Break 32.0 MPa
4640 psi
ISO 527-1/-2
Tensile Stress 4.50 MPa

@Strain 5.00 %
 653 psi

@Strain 5.00 %
 ISO 527-1/-2
6.70 MPa

@Strain 10.0 %
 972 psi

@Strain 10.0 %
 ISO 527-1/-2
11.8 MPa

@Strain 50.0 %
 1710 psi

@Strain 50.0 %
 ISO 527-1/-2
14.0 MPa

@Strain 100 %
 2030 psi

@Strain 100 %
 ISO 527-1/-2
23.0 MPa

@Strain 300 %
 3340 psi

@Strain 300 %
 ISO 527-1/-2
1.87 MPa

@Strain 5.67 %,
Temperature 120 °C
 271 psi

@Strain 5.67 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
2.23 MPa

@Strain 5.69 %,
Temperature 100 °C
 323 psi

@Strain 5.69 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
2.38 MPa

@Strain 5.57 %,
Temperature 90.0 °C
 345 psi

@Strain 5.57 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
3.07 MPa

@Strain 5.62 %,
Temperature 60.0 °C
 445 psi

@Strain 5.62 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
3.16 MPa

@Strain 5.00 %,
Temperature 23.0 °C
 458 psi

@Strain 5.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
3.24 MPa

@Strain 14.34 %,
Temperature 120 °C
 470 psi

@Strain 14.34 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.67 MPa

@Strain 5.61 %,
Temperature 40.0 °C
 532 psi

@Strain 5.61 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
3.93 MPa

@Strain 23.01 %,
Temperature 120 °C
 570 psi

@Strain 23.01 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.95 MPa

@Strain 14.39 %,
Temperature 100 °C
 573 psi

@Strain 14.39 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
4.31 MPa

@Strain 31.01 %,
Temperature 120 °C
 625 psi

@Strain 31.01 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
4.31 MPa

@Strain 14.09 %,
Temperature 90.0 °C
 625 psi

@Strain 14.09 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
4.60 MPa

@Strain 39.68 %,
Temperature 120 °C
 667 psi

@Strain 39.68 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
4.78 MPa

@Strain 22.42 %,
Temperature 100 °C
 693 psi

@Strain 22.42 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
4.88 MPa

@Strain 51.02 %,
Temperature 120 °C
 708 psi

@Strain 51.02 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
5.12 MPa

@Strain 61.69 %,
Temperature 120 °C
 743 psi

@Strain 61.69 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
5.21 MPa

@Strain 21.95 %,
Temperature 90.0 °C
 756 psi

@Strain 21.95 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
5.23 MPa

@Strain 6.30 %,
Temperature 0.000 °C
 759 psi

@Strain 6.30 %,
Temperature 32.0 °F
 TPE; ISO 11403-1 -2
5.31 MPa

@Strain 31.11 %,
Temperature 100 °C
 770 psi

@Strain 31.11 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
5.36 MPa

@Strain 73.03 %,
Temperature 120 °C
 777 psi

@Strain 73.03 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
5.48 MPa

@Strain 14.2 %,
Temperature 60.0 °C
 795 psi

@Strain 14.2 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
5.59 MPa

@Strain 8.22 %,
Temperature 23.0 °C
 811 psi

@Strain 8.22 %,
Temperature 73.4 °F
 TPE; ISO 11403-1 -2
5.60 MPa

@Strain 84.36 %,
Temperature 120 °C
 812 psi

@Strain 84.36 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
5.67 MPa

@Strain 39.81 %,
Temperature 100 °C
 822 psi

@Strain 39.81 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
5.80 MPa

@Strain 30.47 %,
Temperature 90.0 °C
 841 psi

@Strain 30.47 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
5.92 MPa

@Strain 6.08 %,
Temperature -20.0 °C
 859 psi

@Strain 6.08 %,
Temperature -4.00 °F
 TPE; ISO 11403-1 -2
5.97 MPa

@Strain 101.04 %,
Temperature 120 °C
 866 psi

@Strain 101.04 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.01 MPa

@Strain 50.52 %,
Temperature 100 °C
 872 psi

@Strain 50.52 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
6.17 MPa

@Strain 38.34 %,
Temperature 90.0 °C
 895 psi

@Strain 38.34 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
6.24 MPa

@Strain 112.37 %,
Temperature 120 °C
 905 psi

@Strain 112.37 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.31 MPa

@Strain 61.89 %,
Temperature 100 °C
 915 psi

@Strain 61.89 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
6.57 MPa

@Strain 49.48 %,
Temperature 90.0 °C
 953 psi

@Strain 49.48 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
6.58 MPa

@Strain 14.2 %,
Temperature 40.0 °C
 954 psi

@Strain 14.2 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
6.60 MPa

@Strain 126.38 %,
Temperature 120 °C
 957 psi

@Strain 126.38 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.62 MPa

@Strain 73.27 %,
Temperature 100 °C
 960 psi

@Strain 73.27 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
6.66 MPa

@Strain 22.79 %,
Temperature 60.0 °C
 966 psi

@Strain 22.79 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
6.91 MPa

@Strain 60.62 %,
Temperature 90.0 °C
 1000 psi

@Strain 60.62 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
6.92 MPa

@Strain 84.64 %,
Temperature 100 °C
 1000 psi

@Strain 84.64 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
7.08 MPa

@Strain 145.72 %,
Temperature 120 °C
 1030 psi

@Strain 145.72 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.23 MPa

@Strain 71.1 %,
Temperature 90.0 °C
 1050 psi

@Strain 71.1 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
7.35 MPa

@Strain 31.38 %,
Temperature 60.0 °C
 1070 psi

@Strain 31.38 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
7.39 MPa

@Strain 101.37 %,
Temperature 100 °C
 1070 psi

@Strain 101.37 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
7.56 MPa

@Strain 82.24 %,
Temperature 90.0 °C
 1100 psi

@Strain 82.24 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
7.69 MPa

@Strain 168.4 %,
Temperature 120 °C
 1120 psi

@Strain 168.4 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.70 MPa

@Strain 112.08 %,
Temperature 100 °C
 1120 psi

@Strain 112.08 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
7.77 MPa

@Strain 39.31 %,
Temperature 60.0 °C
 1130 psi

@Strain 39.31 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
7.97 MPa

@Strain 22.79 %,
Temperature 40.0 °C
 1160 psi

@Strain 22.79 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
8.08 MPa

@Strain 98.63 %,
Temperature 90.0 °C
 1170 psi

@Strain 98.63 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
8.11 MPa

@Strain 126.13 %,
Temperature 100 °C
 1180 psi

@Strain 126.13 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
8.24 MPa

@Strain 50.54 %,
Temperature 60.0 °C
 1200 psi

@Strain 50.54 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2