Braskem BS 002J HDPE Blow Molding Polyethylene  (discontinued **)

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem BS 002J HDPE Blow Molding Polyethylene  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications: Bottles up to 60 liters with high ESCR; bottles for surface-active agents. Information provided by Braskem
Physical Properties Metric English Comments
Density 0.950 g/cc
0.0343 lb/in³
ASTM D1505
ESCR 100% Igepal® 86 hour

@Thickness 3.00 mm,
Temperature 23.0 °C
 86 hour

@Thickness 0.118 in,
Temperature 73.4 °F
 compression molded plaques; ASTM D1693B
Melt Flow 0.43 g/10 min

@Load 5.00 kg,
Temperature 190 °C
 0.43 g/10 min

@Load 11.0 lb,
Temperature 374 °F
 ASTM D1238
High Load Melt Index 11 g/10 min

@Load 21.6 kg,
Temperature 190 °C
 11 g/10 min

@Load 47.6 lb,
Temperature 374 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 63
63
ASTM D2240
Tensile Strength at Break 32.0 MPa
4640 psi
ASTM D638
Tensile Strength, Yield 26.0 MPa
3770 psi
ASTM D638
Flexural Modulus 1.08 GPa
157 ksi
ASTM D790
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 67.0 °C
153 °F
ASTM D648
Vicat Softening Point 125 °C
257 °F
ASTM D1525