SABIC Innovative Plastics LNP STAT-KON FX98501 PE
| Category | Polymer , Thermoplastic , Polyethylene (PE) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON FX98501 PE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* FX98501 is a compound based on Polyethylene resin containing Proprietary Fillers. Added feature of this material is: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| 1.09 g/cc | 0.0394 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.0100 % | 0.0100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0200 % | 0.0200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 29.0 MPa | 4210 psi | Type I, 5 mm/min; ASTM D638 |
| 32.0 MPa | 4640 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 5 mm/min; ISO 527 |
| 39.0 MPa | 5660 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 7.7 % | 7.7 % | 5 mm/min; ISO 527 |
| 8.5 % | 8.5 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 5.6 % | 5.6 % | 5 mm/min; ISO 527 |
| 5.8 % | 5.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.73 GPa | 396 ksi | 1 mm/min; ISO 527 |
| 3.34 GPa | 484 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 45.0 MPa | 6530 psi | ISO 178 |
| Flexural Modulus | 2.23 GPa | 323 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.35 GPa | 341 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.51 J/cm | 2.83 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.41 J/cm | 10.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 31.0 kJ/m² | 14.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J @Temperature 23.0 °C |
8.11 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 91.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
50.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 129 µm/m-°C @Temperature -30.0 - 30.0 °C |
71.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 118 °C @Thickness 3.20 mm |
244 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 88.0 °C @Thickness 3.20 mm |
190 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 2.0 - 4.0 ohm | 2.0 - 4.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Techmer ES Plaslube® J-1850/30/TF/15 PBT, 30% GFR, 15% PTFE
- Samsung Cheil Industries Starex® SG-301 Expandable Polystyrene (EPS) High Expansion
- Techmer ES HiFill® PP GF50 CC HF BK 50% Glass Filled
- Lubrizol Isoplast® 101LGF60BLK Engineering Thermoplastic Polyurethane Resin
- Polyram PlusTek RA300G4 Nylon 6.6, 20% Glass Fiber
- Arkema Group Lucalor® PEY 333 CPVC, Pipe Grade
- BASF Capron® 8233G 33% Glass-Filled Nylon 6 (Conditioned) (discontinued **)
- Huntsman PE1203 EVA Film Extrusion (discontinued **)
- Unipetrol PP MONSTEN® FC 110 Polypropylene Homopolymer
Copyright © lookpolymers.com All Rights Reserved