SABIC Innovative Plastics LNP STAT-KON FD000 PE
| Category | Polymer , Thermoplastic , Polyethylene (PE) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON FD000 PE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* FD000 is an unfilled Polyethylene. Added feature of this grade is: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0200 % | 0.0200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.020 cm/cm @Time 86400 sec |
0.010 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 31.0 MPa | 4500 psi | 5 mm/min; ISO 527 |
| 32.0 MPa | 4640 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | 5 mm/min; ISO 527 |
| 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 6.5 % | 6.5 % | 5 mm/min; ISO 527 |
| 9.0 % | 9.0 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 5.5 % | 5.5 % | 5 mm/min; ISO 527 |
| 6.1 % | 6.1 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 1.40 GPa | 203 ksi | 1 mm/min; ISO 527 |
| 2.22 GPa | 322 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 30.0 MPa | 4350 psi | ISO 178 |
| Flexural Modulus | 1.30 GPa | 189 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.190 J/cm | 0.356 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.90 J/cm | 16.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 53.0 kJ/m² | 25.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J @Temperature 23.0 °C |
9.59 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 14.0 J | 10.3 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 114 µm/m-°C @Temperature -30.0 - 30.0 °C |
63.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 111 µm/m-°C @Temperature -30.0 - 30.0 °C |
61.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 90.0 °C @Thickness 3.20 mm |
194 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.0 °C | 124 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 51.0 °C @Thickness 3.20 mm |
124 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.0 - 3.0 ohm | 1.0 - 3.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- MV Labs BA890 BaCrO4 Barium chromate
- MV Labs NI250 {Ni(NH3)6}Br2 Hexaminenickel(II) bromide
- Polimeri Europa EDISTIR N1841 Polystyrene (discontinued **)
- Fainplast Compounds RE 620 Rigid PVC, Extrusion
- SABIC Innovative Plastics PC0800 PC
- Samsung Cheil Industries Infino® NH-1035 PC, Unreinforced FR
- Williams Advanced Alloys WS118 Solder
- Chi Mei Polylac® PA-717C ABS
- AKG Polymers Vision PP PPC BL3006 Polypropylene Copolymer Compound
- BASF Novolen® 1101 P Polypropylene
Copyright © lookpolymers.com All Rights Reserved