Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527 |
Nilit FRIANYL A63 W-GV25 Nylon 6.6, std. viscosity for injection molding, 25% glass fiber reinforced Nylon 6.6, std. viscosity for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527 |
Nilit FRIANYL B63 TF-GV 1530 Nylon 6 for injection molding, 15% PTFE lubricated, 30% glass fiber reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Strength at Break | <= 150 MPa | <= 21800 psi | ISO/R527 |
Polykemi AB SCANAMID 66 A12^ F20 FR6 Nylon 66, Glass Fiber Reinforced, Flame Retardant Information provided by Polykemi AB |
|||
Tensile Strength at Break | >= 150 MPa | >= 21800 psi | 50 mm/min; ISO 527-1,2 |
Qualchem Danamid AFGFH-30 Polyamide 66, 30% Glass Fiber Reinforced with glass fiber. Heat stabilized, for long-lasting use at 120-140°C.Information provided by Qualchem Zrt. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527 |
Nilit FRIANYL B63 HS-GV35 Nylon 6 for injection molding, 35% glass fiber reinforced Nylon 6 for injection molding, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527-1/-2 |
DSM Akulon® Ultraflow™ K-FKGS6 Nylon 6-30% Glass Reinforced (European and Asian Grade) (Dry)
(discontinued ** The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ASTM D683 |
Loxim 330 01V0 Nylon 6 Information provided by Loxim Industries |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | Conditioned; ISO 527-1/-2 |
Lanxess Durethan® DP BKV 60 H2.0 EF 900116 Nylon 6, 60% Glass Fiber PA 6, injection molding grade, 60% glass fibers, low viscosity, good flowability (Easy Flow), good heat-resistanceApplication Examples: gearbox housings, spring holders, automotive door handles |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527 Type 1A |
Solvay TECHNYL® A 60 G1 V30 PA66, 30% glass fiber, DRY Description: Flame retardant Polyamide PA66 reinforced with 30% of glass fiber, for injection molding.Available in: Asia Pacific, Europe, Latin America and North AmericaProduct Applications: This R.. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DC006ER PC (Asia Pacific) LNP THERMOCOMP* DC006ER is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527 Type 1A |
Solvay TECHNYL® A 218 V35 Black 34 NG PA66, 35% glass fiber, Conditioned Description: TECHNYL® A 218 V35 Black 34 NG is a polyamide 66, reinforced with 35% of glass fiber, heat stabilized, for injection molding. The product is available in black color.Benefits: This p.. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP QFL36 PA 6/10 LNP LUBRICOMP* QFL36 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DE006ER PC LNP STAT-KON* DE006ER is a compound based on Polycarbonate resin containing 30% Carbon Fiber. Added features of this material include: Easy Molding. Mold Release, Electrically Conductive. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ASTM D638 |
A. Schulman SCHULAMID® 66 GF30H 30% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527-1/-2 |
Unitika A1030GFL45 PA6, 45% Glass Fiber Reinforced, Conditioned Information provided by Unitika Ltd. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527-93 |
Wellman Wellamid® GF25-66 XE-N 25% Glass Fiber Reinforced, Engineering Grade Nylon 66 Description: Glass Fiber Reinforced, Engineering Grade Nylon 66Information provided by Wellman. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527-1/-2 |
DSM Akulon® S223-HPG5 Impact Modified Nylon 66-25% Glass Reinforced (European Grade) (Dry) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® HT XE 3996 PA*-GF30 Product description: Grivory XE 3996 black 9225 is a 30% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. ISO-Polymer designatio.. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® TSG-50 FA PA666-GF50 Information provided by EMS Grivory |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® XE 4106 black 9992 PA612-GF30 Product description: Grilamid XE 4106 black 9992 is a 30% glass fiber reinforced, heat stabilized polyamide 612 injection molding grade. The main features of Grilamid XE 4106 are: low water absorpti.. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® RS 32CG20HSL BK409 Nylon 610
(Unverified Data**) 20% Carbon/Glass Reinforced Renewably Sourced Polyamide 610 Information provided by DuPont Performance Polymers |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | 5 mm/min; ISO 527 |
Eurostar Starflam AFR450B1 PA66, Glass Fiber Reinforced, Flame Retardant, Injection Molding Starflam AFR450B1 is a Flame Retardant, Glass Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | 5 mm/min; ISO 527 |
Eurostar Starflam PF0069 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded Starflam PF0069 is a Flame Retardant, Glass Fiber Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | |
LATI Latilub 66-15ST G/30 PA66, 30% Glass Fiber Reinforced, Silicone/PTFE Filled Self-lubricating product based on Polyamide 66 (PA66). Silicone / PTFE. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by La.. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOTUF PF00AIS PA 6 LNP THERMOTUF* PF00AIS is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 150 MPa | 21800 psi | 5 mm/min; ISO 527-1,-2 |
Lanxess Durethan® AKV 25 F30 000000 Nylon 66, 25% Glass Fiber PA 66, 25% glass fiber, injection molding, flame retardantInformation provided by LANXESS. |
|||
Tensile Strength at Break | 150 MPa @Temperature 1100 °C |
21800 psi @Temperature 2010 °F |
|
Special Metals UDIMET® alloy L-605 Co-Cr-W-Ni Alloy UDIMET® alloy L-605 (UNS R30605) is a solid solution strengthened cobalt-chromium-tungsten-nickel alloy with excellent high-temperature strength and excellent oxidation resistance to 2000°F (1093°.. |