Wellman Wellamid® GF25-66 XE-N 25% Glass Fiber Reinforced, Engineering Grade Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Carbon Fiber Filled |
| Manufacturer | Wellman Engineering Resins |
| Trade Name | Wellamid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wellman Wellamid® GF25-66 XE-N 25% Glass Fiber Reinforced, Engineering Grade Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Glass Fiber Reinforced, Engineering Grade Nylon 66Information provided by Wellman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183-87 |
| Filler Content | 25 % | 25 % | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ISO DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.012 cm/cm | 0.0090 - 0.012 in/in | ISO DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527-93 |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527-93 |
| Flexural Strength | 220 MPa | 31900 psi | ISO 178-93 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 7.86 kJ/m² | 3.74 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75-93 |
Users viewing this material also viewed the following:
- Northstar Polymers MPC-026 Isocyanate prepolymer
- LG Chemical LUPOL TE5007B PP+Rubber, High Impact
- Chase Plastics CP Pryme® N330L (Dry) Nylon 6, 30% Glass Fiber Reinforced, Lubricated, Recycled Content
- Hexcel® HexWeb® CR-PAA™ 1/4-5052-0.001 Phosphoric Acid Anodized Aluminum Honeycomb
- DuPont Performance Polymers Crastin® SK692FR BK507 Polybutylene Terephthalate (PBT) (Unverified Data**)&l
- DuPont Performance Polymers Hytrel® 4068FG Polyester Elastomer TPC-ET (Unverified Data**)
- EMS-Grivory Grivory® GV-2 FWA black 9225 PA*-GF20
- Arlon R32521R010 0.0095" (0.241 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Beijing Ranger Chem SM-634H Semi Solid Epoxy Resin
- BASF TEHA Tris-(2-ethylhexyl)amine
Copyright © lookpolymers.com All Rights Reserved