- Unitika A1030GFL45 PA6, 45% Glass Fiber Reinforced, Conditioned
Unitika A1030GFL45 PA6, 45% Glass Fiber Reinforced, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika A1030GFL45 PA6, 45% Glass Fiber Reinforced, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| Water Absorption | 1.0 % @Time 86400 sec |
1.0 % @Time 24.0 hour |
ISO 62 |
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Thickness 3.20 mm |
0.0010 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm @Thickness 3.20 mm |
0.0030 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 109 | 109 | ISO 2039 |
| Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527-1/-2 |
| Elongation at Break | 4.9 % | 4.9 % | ISO 527-1/-2 |
| Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527-1/-2 |
| Flexural Strength | 220 MPa | 31900 psi | ISO 178 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | ISO 178 |
| Charpy Impact Unnotched | 9.20 J/cm² | 43.8 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 2.30 J/cm² | 10.9 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 23.0 µm/m-°C | 12.8 µin/in-°F | ISO 11359-2 |
| Flammability, UL94 | HB @Thickness 0.860 mm |
HB @Thickness 0.0339 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 7.00e+11 ohm-cm | 7.00e+11 ohm-cm | IEC 60093 |
| Dielectric Strength | 40.2 kV/mm @Thickness 1.00 mm |
1020 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.012 @Frequency 1.00e+6 Hz |
0.012 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 550 V | 550 V | IEC 60112 |
Users viewing this material also viewed the following:
- Kolon SPESIN® KP513FLBL Multi Reinforced PBT Resin (discontinued **)
- SABIC Innovative Plastics Cycoloy® C1110HF PC+ABS (Asia Pacific)
- Multibase Multi-Flex® A 8502 LC TPE Thermoplastic Elastomer
- Techmer ES HiFill® PA6/6 CM25 HS BK 25% Mineral Filled
- Solvay SOPROPHOR® 4 D 384 Surfactant
- Cheng Yu Plastic N6C2 Nylon 6, 20% Mineral Reinforced
- Ensinger Tecast Vekton™ 6PAL Oil-Filled Cast Nylon 6 (PA6)
- 3M FV230 Soft Yellow Vinyl Label Products
- PolyOne Edgetek® AT-5GB/000 Acetal-Copolymer, Glass Bead Filled (discontinued **)
- Quadrant EPP Semitron® ESd 500 HR PTFE, static dissipative, compression molded (ASTM Product Data Sheet)
Copyright © lookpolymers.com All Rights Reserved