Qualchem Danamid AFGFH-30 Polyamide 66, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Qualchem Zrt. |
| Trade Name | Danamid |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Qualchem Danamid AFGFH-30 Polyamide 66, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Reinforced with glass fiber. Heat stabilized, for long-lasting use at 120-140°C.Information provided by Qualchem Zrt.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | DIN 53479 |
| Filler Content | 28 - 32 % | 28 - 32 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | >= 150 MPa | >= 21800 psi | 50 mm/min; ISO 527-1,2 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-1,2 |
| Tensile Modulus | >= 9.30 GPa | >= 1350 ksi | ISO 527-1,2 |
| Charpy Impact Unnotched | >= 2.50 J/cm² @Temperature 23.0 °C |
>= 11.9 ft-lb/in² @Temperature 73.4 °F |
DIN 53453 |
| Charpy Impact, Notched | >= 0.600 J/cm² @Temperature -20.0 °C |
>= 2.86 ft-lb/in² @Temperature -4.00 °F |
DIN 53453 |
| >= 0.800 J/cm² @Temperature 23.0 °C |
>= 3.81 ft-lb/in² @Temperature 73.4 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 4.00 mm |
HB @Thickness 0.157 in |
MSZ 10383 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | DIN 53482 |
| Comparative Tracking Index | 500 V | 500 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Moisture Content | 1.5 - 1.8 % | 1.5 - 1.8 % | DIN 53714 |
Users viewing this material also viewed the following:
- Nabaltec NABALOX® NO 713-10 RF Reactive Alumina
- Kazanorgsintez 276-288 High Density Polyethylene Composite
- Kolon KOCETAL® GF302 G/F Reinforced Acetal Resin
- Solvay Specialty Polymers Diofan® A 050 Polyvinylidene Chloride (PVDC)
- SABIC Innovative Plastics Valox® ENH4550 PBT (Europe-Africa-Middle East)
- Styron INSPIREâ„¢ TF0808S(U) Polypropylene
- Sharadaa Ceramics MULL Mullite
- Ecomass® 1050CO94 Copper Filled Polyamide
- Arlon LW301Rxx-P1 0.030" (0.762 mm) Self-Fusing Silicone Tape (Triangular, Unsupported) with Poly Interleave
- KKPC KOSYN KTR 601 Thermoplastic Elastomer (TPE)
Copyright © lookpolymers.com All Rights Reserved