Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 160 MPa | 23200 psi | ASTM D790 |
NHEP Spectron™ E6126 Nylon 66, 20% Glass Fiber Natural color. E6126 exhibits high rigidity, mechanical strength, and excellent appearance. It is suitable for wide range of applications.Property data measured at room temperature, 50% RH.Informati.. |
|||
Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
Nilit FRIANYL B63 CV10 Nylon 6.6 for injection molding, 10% carbon fiber reinforced Nylon 6.6 for injection molding, good conductive and electrostatic properties.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
Nilit FRIANYL B63 SG-GV20 Nylon 6 for injection molding, 20% glass fiber reinforced Nylon 6 for injection molding, light impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Strength | <= 160 MPa | <= 23200 psi | ISO 178 |
Polykemi AB POLYshine PBT D231 GF15 PBT, Glass-Fiber Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 160 MPa @Temperature 23.0 °C |
23200 psi @Temperature 73.4 °F |
ISO 178 |
DuPont Performance Polymers Crastin® LW9030FR BK851 PBT
(Unverified Data**) Crastin® LW9030FR BK851 is a 30% glass fiber reinforced, flame retardant, black polybutylene terephthalate alloy for injection molding. It has improved surface aesthetics, excellent dimensional sta.. |
|||
Flexural Strength | 160 MPa | 23200 psi | ASTM D790 |
Ravago Manufacturing Americas Enviramid™ N1315HL BK Post Consumer Recycle Nylon 66, 15% Glass Filled Heat Stabilized, Lubricated, Black, and made from EnViramid™ Post Consumer Recycled NylonInformation provided by Ravago. |
|||
Flexural Strength | 160 MPa | 23200 psi | ASTM D790 |
Ravago Manufacturing Americas Enviramid™ N2330 HL BK Post Consumer Recycle Nylon 6, 30% Glass Filled Heat Stabilized, Lubricated, Black and made from EnViramid™ Post Consumer Recycled NylonInformation provided by Ravago. |
|||
Flexural Strength | 160 MPa | 23200 psi | |
Lehmann & Voss LUVOCOM® 1105-8158 PEEK, with mineral filler Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precisio.. |
|||
Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
Idemitsu Kosan Xarec® WA 204 SPS, 20% Glass Filled Crystalline Polymer, Glass Filled, Impact Modified. Used in Automotive and Industrial applications. |
|||
Flexural Strength | 160 MPa | 23200 psi | 1.3 mm/min; ASTM D790 |
Lavergne VYPET VNT 335 PET 35% Glass - Mineral Reinforced Vypet VNT 335 is a 35% glass/mineral reinforced PET injection molding compound designed for structural applications.Features: High temperature performance; Low warp; Excellent dimensional stabilityT.. |
|||
Flexural Strength | 160 MPa | 23200 psi | ASTM D790 |
Gromax PBT 3020-104 15% Glass Fiber Filled Product Description: A glass fiber 20% reinforced injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature Excellent .. |
|||
Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-KON DEL33EC PC LNP STAT-KON* DEL33EC is a compound based on Polycarbonate resin containing 15% Carbon Fiber, 15% PTFE. Added features include: Clean Compounding System, Electrically Conductive, Wear Resistant, Ea.. |
|||
Flexural Strength | 160 MPa | 23200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® DR48V PBT (Europe-Africa-Middle East) VALOX DR48V is a 17% glass reinforced, flame retardant injection moulding PBT resin. Applications: lamp sockets, connectors, switches, electrical housings and bases, bobbins, trimmers and electromot.. |
|||
Flexural Strength | 160 MPa | 23200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON EX01696C PEI LNP* STAT-KON* EX01696C is a compound based on Polyetherimide resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Clean Compounding System. |
|||
Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-KON KE004 Acetal Copoly (Asia Pacific) LNP* Stat-kon* KE004 is a compound based on Acetal Copolymer resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Flexural Strength | 160 MPa | 23200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON Lexan_LCF1506 PC (Europe-Africa-Middle East) LNP* Stat-kon* Lexan_LCF1506 is a 15% carbon fiber, 6% PTFE reinforced polycarbonate. |
|||
Flexural Strength | 160 MPa | 23200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP WF0049 PBT (Europe-Africa-Middle East) LNP* Thermocomp* WF0049 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant. |
|||
Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
Borealis Xmod™ GB305HP High Performance 35% Glass Fiber Reinforced Xmod GB305HP is reinforced with 35% chemically coupled glass fibers and based on a specific Polymer matrix material that is bringing excellent mechanical properties (biaxial impact behavior) as well.. |
|||
Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
Unitika A1030GFL PA6, 30% Glass Fiber Reinforced, Conditioned Information provided by Unitika Ltd. |
|||
Flexural Strength | 160 MPa | 23200 psi | ISO 178-93 |
Wellman EcoLon® MRGF1878-BKJA6A Nylon 6, 30% Mineral/Glass Reinforced Ford JA6A color matchedAll information provided by Wellman Engineered Resins. |
|||
Flexural Strength | 160 MPa | 23200 psi | ASTM-D790 |
Polyram RamShine PW300G7 SAN, 35% Glass Fiber 35% glass fiber reinforced SAN for very high rigidity injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
Polyplastics Duranex® 3105A Polybutylene Terephthalate (PBT), Epoxy adhesion improved, 15% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Flexural Strength | <= 160 MPa | <= 23200 psi | dry, 3.5% flexure; ISO 178 |
Azoty Tarnow™ Tarnamid® T-27 GF15 I Polyamide 6 - Glass Fiber Reinforced 15% Glass fiber reinforced, impact modified, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following mai.. |
|||
Flexural Strength | 160 MPa | 23200 psi | ASTM D790 |
Beijing Ranger Chem PBT-201-G15 272 Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin.. |
|||
Flexural Strength | 160 MPa | 23200 psi | 2.6 mm/min; ASTM D790 |
BLUESTAR LXS 314 G30 PPE-HIPS, 30% Glass Filled Typical Applications: Water industrial partsInformation provided by Polymer Technology and Services, LLC (PTS). |
|||
Flexural Strength | 160 MPa | 23200 psi | At Rupture; ASTM D790 |
Sumitomo Bakelite North America TEM 9053C Hardware Grade Epoxy Short fiberglass and mineral filled, toughened epoxy molding compound with excellent dimensional stability and high strength properties.Information provided by Vyncolit, a Sumitomo Bak Group |
|||
Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
Solvay Specialty Polymers Amodel® A-1422 LS WH 171 Polyphthalamide (PPA)
(discontinued **) Amodel A-1422 LS is a light-stabilized, high-reflectivity, 22%-reinforced white polyphthalamide (PPA) that exhibits high heat resistance, high strength and stiffness over a broad temperature range, .. |
|||
Flexural Strength | 160 MPa | 23200 psi | ASTM D790 |
SABIC Innovative Plastics Lexan® LC108 PC (Asia Pacific) Polycarbonate base, 8% carbon fiber reinforced, FR |