SABIC Innovative Plastics LNP STAT-KON KE004 Acetal Copoly (Asia Pacific)

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Carbon Fiber Filled
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP STAT-KON
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP STAT-KON KE004 Acetal Copoly (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Stat-kon* KE004 is a compound based on Acetal Copolymer resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.

Physical Properties	Metric	English	Comments
Density	1.47 g/cc	0.0531 lb/inÂ³	ASTM D792
	1.47 g/cc	0.0531 lb/inÂ³	ISO 1183
Moisture Absorption	0.200 %	0.200 %	50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.0069 cm/cm @Time 86400 sec	0.0069 in/in @Time 24.0 hour	ISO 294
	0.0060 - 0.0080 cm/cm @Time 86400 sec	0.0060 - 0.0080 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.016 - 0.018 cm/cm @Time 86400 sec	0.016 - 0.018 in/in @Time 24.0 hour	ASTM D955
	0.017 cm/cm @Time 86400 sec	0.017 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	110 MPa	16000 psi	ISO 527
	121 MPa	17500 psi	ASTM D638
Tensile Strength, Yield	110 MPa	16000 psi	ISO 527
	121 MPa	17500 psi	ASTM D638
Elongation at Break	1.4 %	1.4 %	ISO 527
	1.6 %	1.6 %	ASTM D638
Elongation at Yield	1.4 %	1.4 %	ISO 527
	1.6 %	1.6 %	ASTM D638
Tensile Modulus	12.99 GPa	1884 ksi	1 mm/min; ISO 527
	14.47 GPa	2099 ksi	50 mm/min; ASTM D638
Flexural Strength	151 MPa	21900 psi	ASTM D790
	160 MPa	23200 psi	ISO 178
Flexural Modulus	11.03 GPa	1600 ksi	ASTM D790
	11.5 GPa	1670 ksi	ISO 178
Izod Impact, Notched	0.480 J/cm	0.899 ft-lb/in	ASTM D256
Izod Impact, Unnotched	4.27 J/cm	8.00 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	5.00 kJ/mÂ²	2.38 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	25.0 kJ/mÂ²	11.9 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	10.0 J	7.38 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	2.00 J	1.48 ft-lb	Multiaxial Impact; ISO 6603

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	68.4 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	38.0 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	69.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	38.3 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
CTE, linear, Transverse to Flow	30.6 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	17.0 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	31.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	17.2 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	163 Â°C	325 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
	162 Â°C @Thickness 3.20 mm	324 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	160 Â°C	320 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	160 Â°C @Thickness 3.20 mm	320 Â°F @Thickness 0.126 in	unannealed; ASTM D648

Electrical Properties	Metric	English	Comments
Surface Resistance	1.00e+9 - 1.00e+14 ohm	1.00e+9 - 1.00e+14 ohm	ASTM D257