- SABIC Innovative Plastics LNP STAT-KON DEL33EC PC
SABIC Innovative Plastics LNP STAT-KON DEL33EC PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DEL33EC PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DEL33EC is a compound based on Polycarbonate resin containing 15% Carbon Fiber, 15% PTFE. Added features include: Clean Compounding System, Electrically Conductive, Wear Resistant, Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.150 % | 0.150 % | 50% RH, 24 hrs; ASTM D570 |
| 0.210 % | 0.210 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Time 86400 sec |
0.0010 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0014 cm/cm @Time 86400 sec |
0.0014 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0046 cm/cm @Time 86400 sec |
0.0046 in/in @Time 24.0 hour |
ISO 294 |
| 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 96.0 MPa | 13900 psi | ISO 527 |
| 97.0 MPa | 14100 psi | ASTM D638 | |
| Elongation at Break | 3.2 % | 3.2 % | ASTM D638 |
| 3.4 % | 3.4 % | ISO 527 | |
| Tensile Modulus | 7.89 GPa | 1140 ksi | 1 mm/min; ISO 527 |
| 8.48 GPa | 1230 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 159 MPa | 23100 psi | ASTM D790 |
| 160 MPa | 23200 psi | ISO 178 | |
| Flexural Modulus | 7.30 GPa | 1060 ksi | ASTM D790 |
| 7.84 GPa | 1140 ksi | ISO 178 | |
| Izod Impact, Notched | 0.840 J/cm | 1.57 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.15 J/cm | 7.77 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² | 15.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 15.0 J | 11.1 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 18.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
10.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 18.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
10.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 46.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 46.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 146 °C | 295 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P2840 TPE, PP Overmold or Standalone use
- Manifattura Cattaneo PVC U Polyvinyl Chloride
- MetalTek MTEK 430 Martensitic Stainless Steel
- SABIC Innovative Plastics LNP LUBRICOMP EP003 PEI
- SABIC Innovative Plastics ULTEM 2110R PEI
- Borealis MG302Al Polypropylene Compound, Mineral Filled
- 3M FM291 Indoor UL Recognized Clear Polyester Overlaminate Label Products
Copyright © lookpolymers.com All Rights Reserved