- Styrene Acrylonitrile (SAN), Molded, Glass Reinforced
- Polyram RamShine PW300G7 SAN, 35% Glass Fiber
Polyram RamShine PW300G7 SAN, 35% Glass Fiber
| Category | Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded, Glass Reinforced |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamShine PW300G7 SAN, 35% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
35% glass fiber reinforced SAN for very high rigidity injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | DIN 53479 |
| Water Absorption | 0.10 % | 0.10 % | DIN 53495 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | |
| Melt Flow | 9.0 g/10 min @Load 10.0 kg, Temperature 200 °C |
9.0 g/10 min @Load 22.0 lb, Temperature 392 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 94 | 94 | ASTM-D785 |
| Tensile Strength, Yield | 110 MPa | 16000 psi | ASTM-D638 |
| Elongation at Break | 1.5 % | 1.5 % | ASTM-D638 |
| Flexural Strength | 160 MPa | 23200 psi | ASTM-D790 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.650 J/cm @Temperature 23.0 °C |
1.22 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | DIN 53482 |
| Dielectric Constant | 3.1 @Frequency 1e+6 Hz |
3.1 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM PP 4210L (EP2C30F) Propylene and Ethylene Copolymer
- Phillips Sumika Marlex® CBF-300 Talc-Filled High Flow Thermoplastic Olefin (discontinued **)
- Victrex® Vicote® F804 Black Polyetheretherketone (PEEK) Liquid Dispersion
- DuPont Performance Polymers Zytel® 73G45 BK263 Nylon 6 (Unverified Data**)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 45 PHR N990 Filler
- Compuestos Dominicanos Polycom BD-330699 PVC Compound
- Daikin NEOFLON EC-6820 ETFE Coating Powder, White
- Axiall 8835 Moldings & Extrusions Flexible PVC
- Beijing Evergrow Resources Polypropylene Activated Carbon
Copyright © lookpolymers.com All Rights Reserved