Lavergne VYPET VNT 335 PET 35% Glass - Mineral Reinforced
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Glass/Mineral Reinforced |
| Manufacturer | Lavergne Performance Compounds |
| Trade Name | VYPET |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lavergne VYPET VNT 335 PET 35% Glass - Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Vypet VNT 335 is a 35% glass/mineral reinforced PET injection molding compound designed for structural applications.Features: High temperature performance; Low warp; Excellent dimensional stabilityTypical Applications: Electrical / Electronic applications; HousingsInformation provided by Bieglo Gmbh for Lavergne Performance Compounds
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 2.00 mm |
0.0050 in/in @Thickness 0.0787 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 2.00 mm |
0.0090 in/in @Thickness 0.0787 in |
ASTM D955 |
| Ash | 35 % | 35 % | ASTM D2854 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 108 MPa | 15700 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 160 MPa | 23200 psi | 1.3 mm/min; ASTM D790 |
| Flexural Modulus | 9.40 GPa | 1360 ksi | 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.600 J/cm @Temperature 23.0 °C |
1.12 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 265 °C | 500 - 509 °F | |
| Middle Barrel Temperature | 265 - 275 °C | 509 - 527 °F | |
| Front Barrel Temperature | 275 - 295 °C | 527 - 563 °F | |
| Nozzle Temperature | 275 - 300 °C | 527 - 572 °F | |
| Melt Temperature | 275 - 300 °C | 527 - 572 °F | |
| Mold Temperature | 95.0 - 120 °C | 203 - 248 °F | |
| Injection Pressure | 55.0 - 85.0 MPa | 7980 - 12300 psi |
Users viewing this material also viewed the following:
- PolyOne Versalloy™ XL 9055X-9 Thermoplastic Elastomer (TPE)
- Pyrotek C-1 Ceramic fiber paper
- SGL Carbon Group PANOX® SM C063 EEA Oxidized Textile Fiber, Crimped staple fiber, For carbon/carbon and spinning
- A. Schulman INVISION™ VX-7060UE Soft Touch Polyolefin Thermoplastic
- Aclo Accutech Polyethylene HD0234G40UVL High Density Glass Reinforced UV Stabilized
- BASF Ultramid® B50L 01 PA6 (Conditioned)
- ConocoPhillips 32 Spectrum Cutting Oil
- Solvay RHODAPON® SB-8208/S STD Surfactant
Copyright © lookpolymers.com All Rights Reserved