- Polymer Property : Flexural Strength = 13900 psi
Polymer Property : Flexural Strength = 13900 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 95.8 MPa | 13900 psi | ASTM D790 |
| Polymer Resources PC-GP3-D-[color]-5 Polycarbonate, FDA-compliant Feedstocks, High Flow Polycarbonate, FDA-compliant Feedstocks, High FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr.. |
|||
| Flexural Strength | 95.8 MPa | 13900 psi | ASTM D790 |
| Polymer Resources PC-UV3-D-[color]-1 Polycarbonate, UV-stabilized, High Flow with Mold Release Polycarbonate, UV-stabilized, High Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informa.. |
|||
| Flexural Strength | 96.1 MPa | 13900 psi | |
| Mitsui AURUM® JNF3020 Thermoplastic Polyimide Resin, Wear/Friction Grade
(discontinued **) AURUM® is an easy melt, processable and recyclable thermoplastic polyimide resin that provides continuous service temperatures to 465° F in its amorphous state and up to 550° F when annealed to i.. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | |
| Lehmann & Voss LUVOCOM® 6-8548 Polyamide 12, with glass fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Suitable for discharging of statically generated electricity.Dynamic stressed parts.Low waterab.. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D 790 |
| MRC Polymers NAXELL™ PC117MH General Purpose Polycarbonate, Medium High MFR • Available in natural and custom colors• Can be UV Stabilized• Internal and external lubricants can be addedInformation provided by MRC Polymers Inc. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D 790 |
| SABIC Innovative Plastics LNP Lubricomp DX99854 PC LNP LUBRICOMP* DX99854 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP.. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP HFG25Z PA 11 LNP* Lubricomp* HFG25Z is a compound based on Nylon 11 resin containing 25% Glass Fiber, 10% Graphite. Added features of this material include: Internally Lubricated. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP IAL12 PA 6/12 (Asia Pacific) LNP* Lubricomp* IAL12 is a compound based on Nylon 6/12 resin containing PTFE, Aramid Fiber. Added features of this material include: Internally Lubricated. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP STAT-KON DD000CEX PC LNP STAT-KON* DD000CEX is a compound based on Polycarbonate resin containing Carbon. Added features of this material include: Clean Compounding System. Easy Molding, Electrically Conductive. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP STAT-KON DX03571 PC LNP* STAT-KON* DX03571 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ISO 178 |
| SABIC Innovative Plastics LNP STAT-KON KX02764 Acetal LNP STAT-KON* KX02764 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP 9X04488 POLYPHENYLENESULFONE (Asia Pacific) LNP* Thermocomp* 9X04488 is a compound based on POLYPHENYLENESULFONE resin containing Mineral. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP 9X04488 PPS LNP* THERMOCOMP* 9X04488 is a compound based on PPS resin containing Mineral. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP CF008 PS (Asia Pacific) LNP* Thermocomp* CF008 is a compound based on Polystyrene resin containing Glass Fiber. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | 2mm/min; ISO 178 |
| Teijin Multilon TN-7500F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. High stiffness and flowability realize the thin wall of large-scale business machine chassis.Information provided by Tei.. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D 790 |
| SABIC Innovative Plastics LNP Thermocomp PH0600A PA 6 LNP THERMOCOMP* PH0600A is a compound based on Nylon 6 resin. Added features of this material include: High Specific Gravity.This data was supplied by SABIC-IP for the Americas region. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D 790 |
| SABIC Innovative Plastics LNP Thermocomp PH0600A PA 6 (Asia Pacific) LNP* THERMOCOMP* PH0600A is a compound based on Nylon 6 resin. Added features of this material include: High Specific Gravity.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP RZ0069 PA 66 (Asia Pacific) LNP* Thermocomp* RZ0069 is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant, Milled Glass. Added features of this material include: Flame Retardant. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ISO 178 |
| SABIC Innovative Plastics LNP STAT-KON 9X02785 PC LNP STAT-KON* 9X02785 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP STAT-KON DX05305C PC LNP* STAT-KON* DX05305C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Clean Compounding System. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP STAT-LOY PF306 PA 6 LNP* STAT-LOY* PF306 is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added feature of this grade includes: Antistat. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D 790 |
| SABIC Innovative Plastics LNP Thermotuf VF002 PA 66 (Asia Pacific) LNP THERMOTUF* VF002 is a compound based on Nylon resin containing Glass Fiber. Added features of this material include: High Impact.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| Plenco 00714 Melamine-Phenolic, Granular, Injection Molded PLENCO 00714 is a melamine-phenolic copolymer molding compound, offering excellent arc resistance and comparative track index values. Type ASTM D 5948 CMG, and UL recognized under component file E4.. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ISO 178 |
| Polyplastics Duracon® TR-20 Acetal Co-polymer (POM), Mineral filling, Mineral filling, High rigidity, Low warpage DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O).. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | Outer Fiber Stress at 3.5% Outer Fiber Strain; DIN EN ISO 178 |
| Wolf Kunststoff ZEDEX® ZX-100K A1K Polymer Alloy Main Characteristics: Hard; Stiff; Tough; High fatigue strength; Good weather resistance; Good machinability; FDA compliant LABS; PTFE and silicone-free; KTW approved; Stress resistantApplications: .. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | |
| Zeon Chemicals Zeonex® 480R Cyclo-Olefin Polymer |
|||
| Flexural Strength | 95.8 MPa | 13900 psi | ASTM D790 |
| Entec Hylex® P1017L1 HB Polycarbonate Available in North America Additive: Mold Release Features: Good Mold Release and High Flow RoHS Compliant Form: Pellets Appearance: Clear/Transparent Information provided by Entec |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| A. Schulman ComAlloy Hiloy® 419 Polyester - PBT, Mineral Reinforced Data provided by the manufacturer, ComAlloy International Company.40% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | GB9341 |
| Beijing Evergrow Resources MC Nylon Information provided by Beijing Evergrow Resources. |
|||
| Flexural Strength | 96.0 MPa | 13900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP AX06472 ABS LNP* Thermocomp* AX06472 is a compound based on ABS containing a clay blend. |
|||