SABIC Innovative Plastics LNP STAT-KON KX02764 Acetal

Category	Polymer , Thermoplastic , Acetal (POM)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP STAT-KON
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP STAT-KON KX02764 Acetal.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP STAT-KON* KX02764 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive.

Physical Properties	Metric	English	Comments
Density	1.43 g/cc	0.0517 lb/inÂ³	ISO 1183
	1.443 g/cc	0.05213 lb/inÂ³	ASTM D792
Moisture Absorption	0.180 %	0.180 %	50% RH, 24 hrs; ASTM D570
	0.250 %	0.250 %	23Â°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.015 - 0.035 cm/cm @Time 86400 sec	0.015 - 0.035 in/in @Time 24.0 hour	ASTM D955
	0.015 - 0.035 cm/cm @Time 86400 sec	0.015 - 0.035 in/in @Time 24.0 hour	ISO 294
Linear Mold Shrinkage, Transverse	0.015 - 0.035 cm/cm @Time 86400 sec	0.015 - 0.035 in/in @Time 24.0 hour	ASTM D955
	0.015 - 0.035 cm/cm @Time 86400 sec	0.015 - 0.035 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	46.0 MPa	6670 psi	ISO 527
	47.0 MPa	6820 psi	ASTM D638
Tensile Strength, Yield	53.0 MPa	7690 psi	ASTM D638
	53.0 MPa	7690 psi	ISO 527
Elongation at Break	10.2 %	10.2 %	ASTM D638
	18.1 %	18.1 %	ISO 527
Elongation at Yield	3.8 %	3.8 %	ASTM D638
	4.0 %	4.0 %	ISO 527
Tensile Modulus	3.46 GPa	502 ksi	1 mm/min; ISO 527
	3.48 GPa	505 ksi	50 mm/min; ASTM D638
Flexural Strength	96.0 MPa	13900 psi	ISO 178
	100 MPa	14500 psi	ASTM D790
Flexural Modulus	3.01 GPa	437 ksi	ASTM D790
	3.01 GPa	437 ksi	ISO 178
Izod Impact, Notched	0.420 J/cm	0.787 ft-lb/in	ASTM D256
Izod Impact, Unnotched	3.73 J/cm	6.99 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	4.00 kJ/mÂ²	1.90 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	52.0 kJ/mÂ²	24.7 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	3.00 J	2.21 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	7.00 J	5.16 ft-lb	Multiaxial Impact; ISO 6603

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	103 Â°C	217 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	106 Â°C @Thickness 3.20 mm	223 Â°F @Thickness 0.126 in	unannealed; ASTM D648

Electrical Properties	Metric	English	Comments
Volume Resistivity	100 - 1.00e+6 ohm-cm	100 - 1.00e+6 ohm-cm	ASTM D257
Surface Resistance	100 - 1.00e+6 ohm	100 - 1.00e+6 ohm	ASTM D257